The tribological properties of AlCoCrFeNi and AlCoCrFeNiTi_(0.5) high entropy alloys under gear oil and multiply alkylated cyclopentanes(MACs)lubrication condition have been studied.The equiaxed crystal structure of AlCoCrFeNi alloy is obtained after heat-treatment.The AlCoCrFeNiTi_(0.5) alloy keeps dendrite structure.Under the gear oil with good lubrication action,AlCoCrFeNiTi_(0.5) alloy preserves better tribological properties than AlCoCrFeNi alloy.The delamination and crack behaviors tend to occur in the grain boundary of AlCoCrFeNi alloy and along the interdendrite region of AlCoCrFeNiTi_(0.5) alloy.Under the MACs with relatively poor lubrication action,the applied load slightly influences the wear behavior of AlCoCrFeNi alloy,but seriously impacts the wear mechanism of AlCoCrFeNiTi_(0.5) alloy.Compared with AlCoCrFeNi alloy,AlCoCrFeNiTi_(0.5) alloy keeps better wear-resistance at low applied load of 100 N,but preserves less wearresistance at high applied load of 200 N.
The tribological properties of AlCoCrFeNi and AlCoCrFeNiTi_ (0.5) high entropy alloys under gear oil and multiply alkylated cyclopentanes (MACs) lubrication condition have been studied. The equiaxed crystal structure of AlCoCrFeNi alloy is obtained after heat-treatment. The AlCoCrFeNiTi_ (0.5) (0.5) alloy preserves better tribological properties than AlCoCrFeNi alloy. delamination and crack behaviors tend to occur in grain boundary of AlCoCrFeNi alloy and along the interdendrite region of AlCoCrFeNiTi_ (0.5) alloy.Under the MACs with relatively poor lubrication action, the applied load slightly influences the wear behavior of AlCoCrFeNi alloy, but only affect the wear mechanism of AlCoCrFeNiTi_ (0.5) alloy .Compared with AlCoCrFeNi alloy, AlCoCrFeNiTi_ (0.5) alloys keeps better wear- resistance at low applied load of 100 N, but preserves less wear resistance at high applied load of 200 N.