The influences of quenching speed and current annealing on the magnetic properties of Nd9Fe86B5 ribbons were investigated. There is an optimum quenching speed (v ≈ 15 m/s) for preparing hard magnetic ribbons, where the remanence of 1.22 T, the intrinsic coercivity of 521 kA?m?1 and the energy products of 150 kJ?m?3 are obtained. After annealing ribbons prepared with v = 20 m/s at a dc current of 0.85 A, the remanence reaches a quite large value of 1.47 T, which attributes to the strong exchange coupling interactions between the fine grains of Nd2Fe14B and α-Fe.
The influences of quenching speed and current annealing on the magnetic properties of Nd9Fe86B5 ribbons were investigated. There is an optimum quenching speed (v ≈ 15 m / s) for preparing hard magnetic ribbons, where the remanence of 1.22 T, the intrinsic coercivity of 521 kA? m? 1 and the energy products of 150 kJ? m? 3 are obtained. After annealing ribbons prepared with v = 20 m / s at a dc current of 0.85 A, the remanence reaches a quite large value of 1.47 T, which attributes to the strong exchange coupling interactions between the fine grains of Nd2Fe14B and α-Fe.