采用70℃、3.5%(质量分数)的海盐溶液对不饱和聚酯玻璃钢及环氧乙烯基酯玻璃钢进行加速老化实验,研究了玻璃钢的耐海水腐蚀性能,并对2 mm厚的玻璃钢防护层的抗Cl~-渗透寿命进
【机 构】
：
中交上海三航科学研究院有限公司,上海宏韵新型建材有限公司,
论文部分内容阅读
采用70℃、3.5%(质量分数)的海盐溶液对不饱和聚酯玻璃钢及环氧乙烯基酯玻璃钢进行加速老化实验,研究了玻璃钢的耐海水腐蚀性能,并对2 mm厚的玻璃钢防护层的抗Cl~-渗透寿命进行了预测。结果表明:不饱和聚酯玻璃钢在海水中容易发生水解腐蚀,其抗Cl~-渗透寿命约为30 a;而环氧乙烯基酯玻璃钢的抗Cl~-渗透寿命约为70 a,具有更好的耐海水腐蚀性能。
Accelerated aging experiments of unsaturated polyester fiberglass and epoxy vinyl ester fiberglass with sea salt solution of 70 ℃ and 3.5% (mass fraction) were carried out to study the seawater corrosion resistance of fiberglass, and the corrosion resistance of 2mm thick fiberglass protective layer Anti-Cl ~ - penetration life expectancy was predicted. The results show that unsaturated polyester fiberglass is prone to hydrolytic corrosion in seawater, and its resistance to Cl ~ - infiltration life is about 30 a; while the resistance to Cl ~ - penetration of epoxy vinyl ester fiberglass is about 70 a, which is better Seawater corrosion resistance.
其他文献
蒙山是沂蒙山区的主要板栗产区。近年来 ,板栗生产迅速发展 ,为山区经济的发展奠定了良好的基础。但随着板栗大面积的陆续投产 ,害虫也普遍发生 ,受害较轻的园片产量下降 1 0
目前，常用的网络建模仿真工具有很多，其中OPNET Modeler 的使用最为广泛。本文主要探讨该软件在空间网络建模与仿真中的应用，介绍其主要特点和建模模块及它为空间网络仿真提供的
通过电化学测试、浸泡实验和表面分析技术研究了交流电频率(50~400 Hz)对X80钢在鹰潭酸性土壤模拟溶液中腐蚀行为的影响。结果表明,随交流电频率的增加,X80钢的腐蚀速率逐渐
利用灰关联法分析了原油性质与原油储罐16Mn钢腐蚀行为的关系,并应用层次分析法探讨了原油性质中与腐蚀相关的各因素对16Mn钢腐蚀速率的影响权重.结果表明:原油性质中影响16M
采用周浸实验模拟了A1060纯Al在我国万宁、西沙两种海洋大气环境下的腐蚀行为,用扫描电镜(SEM)、能谱分析(EDS)、X射线衍射(XRD)和失重法等方法研究了A1060纯Al在室内模拟大
本文依据遥感卫星数据接收任务要求，分析研究了多站多星任务调度问题的主要约束条件，提出了优化目标函数，创建了基于约束满足优化问题的多站多星任务调度优化模型。
熔盐反应堆是一种以熔融盐为冷却剂和核燃料的反应堆。作为6种第四代核电站概念堆之一,熔盐堆正日益受到人们的关注。材料的腐蚀问题是熔盐堆发展过程中面临的一个技术挑战。
本文介绍了自主研发的通用的航天任务可视化仿真平台——VisualSpace的设计思想，分析并展示了各核心模块的能力，及各模块在卫星任务可视化仿真中的作用。展示了基于VisualSpace
研究了锻后固溶处理和锻后去应力处理对核电主管道用316LN不锈钢的显微组织、残余应变和常温力学性能的影响,并研究了不同锻后热处理工艺对316LN不锈钢在沸腾的42%(质量分数)
通过动电位极化曲线和静态失重法研究了ZK60镁合金在3.5%卤化钠Na X(X=F,Cl,Br和I)溶液中的腐蚀行为,并且利用SEM观察了ZK60镁合金的腐蚀形貌。结果表明:ZK60镁合金在3.5%Na