【摘 要】
：
9 SiCr钢制字头模要求硬度HRC60～62,原热处理工艺虽能满足一般要求,但字模寿命低有时出现崩刃、掉角、软塌、冲毛等早期失效。被冲压零件硬度一般为HRC 30～45。字模寿命最长为
论文部分内容阅读
9 SiCr钢制字头模要求硬度HRC60～62,原热处理工艺虽能满足一般要求,但字模寿命低有时出现崩刃、掉角、软塌、冲毛等早期失效。被冲压零件硬度一般为HRC 30～45。字模寿命最长为千次,少则百次。原工艺:850℃中温盐浴炉加热,保温30 s/mm,油淬,180±10℃回火1h,空冷。分析认为,造成早期失效的主要原因是:保温时间计算不合理。保温时
9 SiCr steel head die hardness HRC60 ~ 62, although the original heat treatment process to meet the general requirements, but the die life is sometimes low chipping, off angle, soft collapse, red hair and other early failure. Stamping parts hardness is generally HRC 30 ~ 45. The longest mold life of a thousand times, ranging from a hundred times. The original process: 850 ℃ temperature salt bath heating, insulation 30 s / mm, oil quenching, tempering 180 ± 10 ℃ 1h, air-cooled. Analysis, the main reason for the early failure is: insulation time calculation is not reasonable. When insulation
其他文献
金矿开发对于与金矿床有关的元素的早期工作,以地球化学方面更为详细,特别是对于砷、碲、硒和汞的研究。围绕显微细粒金矿床的地球化学模式已得到认识,对现代地热系统中金的
矿物学发展至今,已经出现了不少的分支学科。总起来说,矿物学有三个主要的方向,即矿物晶体化学方向、矿物物理学方向和成因矿物学的方向。其中晶体化学和矿物物理学越向纵深
充分利用长三角路网发达、企业规模大、车辆高档、管理先进、旅客资源丰富等有利条件,协调好路、站、线、车关系,方能突破客运班车进(出)城和上(下)高速难、旅客中转距离远和次数多、高速客运班车途中配载和旅客换乘购票难等三大瓶颈。 高速铁路建设加速了长三角主要城市同城效应的推进,但更多的同城效应还是需要道路运输一体化来实现和保障。如何突破瓶颈,有效发挥相对城际铁路、支线航空而言的点多面广、能够实现全
本文通过正交试验设计了最佳的合金成分,并简要介绍了合金的生产工艺。试验结果明表,该合金具有优良的加工性能,良好的耐蚀性,其表面呈现与18开金相似的金黄色泽。合金初步应
1.工件的坐标测量原理由计算机辅助的工件坐标测量是基于工件表面的数字模型。这个表面数字模型由一确定的坐标系中各种形状要素所构成的一组方程式来表示。对标称工件,方程
在普通车床上加工多品种、形状复杂、工艺性要求高的零件是有一定困难的。这里介绍一种在普通车床上使用的多功能刀架,即能保证工件的加工精度及其他要求,又能提高效率。刀
传统西方政治学研究主要关注两个变量之间的因果性分析。多重因果路径分析是传统二元因果分析的一个延伸，它强调因果链条的重要性，即在传统的自变量和因变量之间可能存在着若干个中介变量。多重因果路径分析分别在定量研究、定性研究以及形式理论中得到了运用。在近来的多重因果路径分析中，几种研究方法开始有融合的趋势，比如定量研究与定性研究的结合，形式理论与定量研究的融合。多重因果路径分析中几种研究方法的融合为政治学研究的发展开辟了新的方向，但其本身也存在局限性。
世界经济的苦恼1982年世界经济自从第二次石油危机以来,已经经过了4年,经历了比七十年代更加严重的困难。例如,发达国家的经济在六十年代,增长率是5%,遭遇两次石油危机的七
本文探讨了真空软氮化工艺参数对渗层特性的影响,并与气体软氮化、真空氮化进行了比较。通过离子探针、扫描电镜、波谱仪、声发射等对渗层C·N含量及分布、相结构、应力状态
一工业发展与劳动生产率战后主要资本主义国家的工业生产都有了较大的增长,而日本是这些国家中增长最快的,由1950年至1977年,日本工业生产增
Industrial Development and L