采用加弧辉光离子渗金属技术，在三种含碳量（０．１％Ｗｔ、０．４５％Ｗｔ、０．８０ｗｔ％）的碳钢试样表面进行了镍－铬共渗处理，对渗层的组织形貌、合金元素成分分布以及其相组成进行了研究，测定了经加孤辉光离子镍－铬共渗处理的试样在０．０５ｍｏｌ／ＬＨ２ＳＯ４溶液中的电位－时间曲线。结果表明，１０钢试样表面形成的镍－格共修层为单一的γ相；４５、Ｔ８钢试样表面形成的镍－铬共渗层是以γ相为基，同时存在碳化物Ｃｒ２３Ｃ６、Ｃｒ７Ｃ３。经加孤辉光离子镍－铬共渗处理后，１０、４５钢试样的表面抗蚀性能大大提高，与１８－８型不锈钢相当；Ｔ８钢试样的表面抗蚀性能没有十分明显的改善。
Nickel-chromium co-infiltration treatment was performed on the surface of three kinds of carbon steel with carbon content (0.1% Wt, 0.45% Wt, 0.80wt%) by adding arc glow ion infiltration metal. The microstructure, composition distribution and phase composition of the alloying elements were investigated. The potential-time curves of the samples treated with lone-glow nickel-chromium co-permeation in 0.05 mol / LH 2 SO 4 solution were determined. The results show that the Ni-grid co-layer formed on the surface of the 10 steel is a single γ phase. 45, the Ni-Cr co-diffusion layer formed on the surface of the T8 steel sample is based on the γ phase with carbide Cr23C6, Cr7C3. The surface corrosion resistance of 10,45 steel samples increased greatly with the addition of glow-glow nickel-chromium co-permeation treatment, which is equivalent to that of 18-8 type stainless steel. The surface corrosion resistance of T8 steel samples was not significantly improved .