论文部分内容阅读
With constant enlargement of the application areas of the spherical plain bearings, higher quality lubrication of the bearings is required. To solve the lubricating problems of spherical plain bearings under high temperature, high vacuum, high speed, heavy loads and strong oxidation conditions, it is urgent for us to develop more excellent self-lubricating technologies. In this paper, the bonded solid lubricant coatings, which use inorganic phosphate as the binder, the mixture of MoS2 and graphite with two different weight proportions as the solid lubricant, are prepared by spraying under three different spray gun pressures. The bonding strength tests on the coatings show that the best spraying pressure is 0.2 MPa and the better mixing proportion of MoS2 to Graphite is 3:1. Then for the radial spherical plain bearings with steel/steel friction pair, after the coatings are made on the inner ring outer surfaces, the friction coefficient, the wear loss and the friction temperature of the bearings under four oscillating frequencies are investigated by a self-made tribo-tester. The test results, SEM of the w morphologies and EDS of w areas show that tribological properties of the bearing are obviously improved by the bonded solid lubricant coatings. When sprayed under the spray gun pressure of 0.2 MPa, the bearings have better anti-friction and anti-wear properties than those sprayed under 0.1 MPa and 0.3 MPa. Further as proved from the XPS analysis, between the coating with 3:1 mixing ratio of MoS2 to Graphite and the coating with 1:1 ratio, the former has less oxidation occurred on the surface and therefore has better tribological characteristics than the latter. This paper provides a reference to developing a new product of the radial spherical plain bearings with high bonding strength, oxidation resistance and abrasion resistance.