【摘 要】
：
Proton ligand stability constants of hydroxybenzoic acid containing nitro group (2-Hydroxy-4-nitrobenzoic acid and 3-Hydroxy-4-nitrobenzoic acid) were determine
论文部分内容阅读
Proton ligand stability constants of hydroxybenzoic acid containing nitro group (2-Hydroxy-4-nitrobenzoic acid and 3-Hydroxy-4-nitrobenzoic acid) were determined through Irving-Rossoti pH titration technique. The stability constants of rare earth metal chelates con-taining 2-Hydroxy-4-nitrobenzoic acid and 3-Hydroxy-4-nitrobenzoic acid as ligands were studied in aqueous medium at different ionic strength (μ=0.01, 0.05 and 0.1 mol/L) and temperatures (298, 308 and 318±0.1 K). The values of stability constant were evaluated through different computational methods like successive approximation, least square treatment, correction term method, and convergence method. The observed value of thermodynamic parameters (△G°, △H° and △S°) favors the complex formation between metal and ligands. The order of stability constant was found to be Pr(Ⅲ)
其他文献
To inhibit chips burning in the high-speed cutting of Ti-6Al-4V, nitrogen gas with 0.7 MPa pressure was ejected at the milling zone. The high speed flowing of n
Zinc phosphate coatings formed on 6061-Al alloy, after dipping in phosphating solutions containing different amounts of Y2O3(yttrium oxide), were studied by sca
Mn segregation at austenite/ferrite interface is studied in a Fe-C-Mn-Si alloy held at 656℃.Mn is partitioned during the growth of ferrite and as a result, a M
TiB2 and Dy2O3 were used as codeposited particles in the preparation of Ni-TiB2-Dy2O3 composite coatings to improve its per-formance. Ni-TiB2-Dy2O3 composite co
Electrical conductivity of NaF-AlF3 melts was measured by continuously varying cell constant(CVCC) technique. Relationships between equivalent conductivity at 9
The TiN/Ti multilayer was deposited on Ti-811 alloy surface by magnetron sputtering(MS) technique for improving fretting fatigue(FF) resistance of the titanium
Three-dimensionally ordered macro-porous(3DOM) TiO2 and ceria-modified 3DOM TiO2 supported platinum catalysts were pre-pared with template and impregnation meth
γ-mercapto-propyl trimethoxysilane (MPTS) and γ-methacryloxy propyltrimethoxysilane (MPTES) were self-assembled on a hy-droxylated glass substrate to form a t
Powdering/exfoliating of coatings and scratching are the main forms of surface damage in the forming of galvanized steels and high strength steels (HSS), which
The transport of Dy(Ⅲ) through a dispersion supported liquid membrane (DSLM) consisting of polyvinylidene fluoride mem-brane (PVDF) as the liquid membrane supp