Owing to the absence of metal binder,binderless cemented carbides have higher wear,corrosion,and oxidation resistance.WC-0.3VC- 0.5Cr_3C_2 powders with an average particle size of 200 nm and a little amount of active element were consolidated by spark plasma sintering. The sintered microstructure revealed that the average WC grain size was 0.24μm,which was almost consistent with the initial fine powder. The results of XRD showed that W_2C phase was formed.Nearly complete densification of ultrafme binderless cemented carbide was achieved by sintering at 1400℃for 120 s under 50 MPa.The resulting hardness and the fracture toughness were 28.18 GPa and 6.05 MPa·m~(1/2),respectively.
Owing to the absence of metal binder, binderless cemented carbides have higher wear, corrosion, and oxidation resistance. WC-0.3VC-0.5Cr_3C_2 powders with an average particle size of 200 nm and a little amount of active element were consolidated by spark plasma sintering . The sintered microstructure revealed that the average WC grain size was 0.24 μm, which was almost consistent with the initial fine powder. The results of XRD showed that W_2C phase was formed. Completely complete densification of ultrafme binderless cemented carbide was achieved by sintering at 1400 ℃ for 120 s under 50 MPa. The resulting hardness and the fracture toughness were 28.18 GPa and 6.05 MPa · m ~ (1/2), respectively.