Al-7%Si-0.2%Mg合金经545℃×7 h+180℃×5 h热处理后,各项性能得到大幅提高,电导率41.28%IACS,抗拉强度240.6 MPa,布氏硬度89.1 HB;过饱和铝基固溶体中析出Mg2Si相和Si相,晶
【机 构】
：
南京航空航天大学,张家界航空工业职业技术学院航空制造工程系,
论文部分内容阅读
Al-7%Si-0.2%Mg合金经545℃×7 h+180℃×5 h热处理后,各项性能得到大幅提高,电导率41.28%IACS,抗拉强度240.6 MPa,布氏硬度89.1 HB;过饱和铝基固溶体中析出Mg2Si相和Si相,晶格畸变程度明显降低,合金的电导率增幅最高可达28.16%,强度提升比例为50.65%,硬度的增幅达55.22%。
After heat treatment at 545 ℃ for 7 h and 180 ℃ for 5 h, the properties of Al-7% Si-0.2% Mg alloy were greatly improved. The electrical conductivity was 41.28% IACS, the tensile strength was 240.6 MPa and the Brinell hardness was 89.1 HB. Mg2Si phase and Si phase precipitated in the supersaturated aluminum-based solid solution, the degree of lattice distortion is obviously reduced. The conductivity of the alloy increases up to 28.16%, the strength increase ratio is 50.65% and the hardness increase rate is 55.22%.
其他文献
厦门市政府有关部门日前公布了2008年厦门市住房建设计划,预计2008年厦门新开工住房建筑面积约为574万平方米。根据该项计划,在新开工住房
Relevant departments of Xiamen
案例分析在人民币持续升值和国家对外商投资房地产的外汇管理政策不断收紧的背景下,我们发现一外商投资的房地产企业在项目筹备阶段,因不具备正常的结汇条件,而不能使用企业
碗莲喜肥。爱莲者该为它准备哪些肥才对它的口味呢?基肥用20%鸟粪、60%园土、20%塘泥或稻田泥搅匀后堆沤。家庭可用缸盛沤。一般从上年11月开始沤制,其间经常灌水,保持一定
近年森林公园建设取得很大发展,为人们接近大自然、走进大自然提供了极好条件。为了丰富人们的休闲生活,增添游憩情趣,争相添置各种体育或游乐设施。有的公园投入重金大搞欧
9月19日至20日，“制度、改革与经济发展”（Institutions，Reformsand Economic Development）大型国际学术研讨会在北京大学经济学院举行。本次论坛由北京大学经济学院与美国新兴市场研究协会（Society forthe Study of Emerging Markets）合作举办，北京大学海外名家讲学计划参与资助。来自24个国家和地区近百位经济学者共襄盛举。
CIOI:你如何看中国寿险行业的整体发展?当前中国寿险行业处于寡头垄断格局。市场排名前6位的保险公司控制了85%的市场份额,而国寿股份和平安寿险则控制了整个寿险市场60%的
巴罗萨位于南澳,于1842年由德国和英国的早期移民建立。巴罗萨有750家葡萄酒农和170家葡萄酒公司,是世界闻名的葡萄酒产区,理想的葡萄酒旅游度假胜地。畅游其间给人带来欢乐
背景正常成人的室间隔分为结构和功能均不相同的左心室面及右心室面两部分,而这两部分在原发性高血压患者会发生怎样的变化尚未见报道。目的探讨室间隔左右心室面在评价原发
目的探讨“套扎法”改良小切口在子宫次全切除术中的应用效果。方法将90例妇科良性疾病患者根据手术方法的不同分为小切口组43例、腹腔镜组47例,小切口组采用“套扎法”改良
排球垫球时屈肘是一种常见错误，分析产生错误的原因，有利于尽快掌握纠正错误的方法，从而学会正确动作。实践中发现，初学垫球的学生几乎全都是屈肘垫球，在教师讲解和示范后，仍有很多