【摘 要】
：
采用失重法、集气法、极化曲线法研究了Sr含量对体育器械用Mg-6Al合金耐腐蚀性能的影响。结果表明,随着Sr含量的增加,合金的腐蚀速率呈增加趋势,但当Sr含量为1%时,合金的腐蚀
论文部分内容阅读
采用失重法、集气法、极化曲线法研究了Sr含量对体育器械用Mg-6Al合金耐腐蚀性能的影响。结果表明,随着Sr含量的增加,合金的腐蚀速率呈增加趋势,但当Sr含量为1%时,合金的腐蚀速率降低。合金耐腐蚀性能提高的主要原因在于晶界处析出Al4Sr相可以有效地抑制腐蚀的扩散。此外,Sr的加入可以促使晶粒细化,使腐蚀均匀性得到提高。
The effects of Sr content on the corrosion resistance of Mg-6Al alloy for sports equipment were studied by weight loss method, gas gathering method and polarization curve method. The results show that with the increase of Sr content, the corrosion rate of the alloy tends to increase, but when the content of Sr is 1%, the corrosion rate of the alloy decreases. The main reason for the improvement of the corrosion resistance of the alloy is that the precipitation of Al4Sr phase at grain boundaries can effectively inhibit the diffusion of corrosion. In addition, the addition of Sr can promote grain refinement, so that corrosion uniformity is improved.
其他文献
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
The pitting corrosion behavior of stainless steel(SS)304in aqueous CO2-H2S-Clenvironment was investigated by potentiodynamic cyclic anodic polarization and elec
前言长期以来,边缘海的地质发展是热烈研究的课题。这些边缘海起因于俯冲带-岛弧-弧后扩张盆地复合体的活动。它包含捕入的边缘海残余和毗邻板块的断块 (Uyeda等,1972;Karig
前言上海是我国经济和文化中心,又是对外开放的大城市,在夏秋季节,它常受到TC(热带气旋)风暴潮的袭击,当天文潮和TC风暴潮相迂达到高潮位时,容易发生灾害,严重威胁着人民生
“十二五”以来,浦东新区围绕“转型驱动、创新发展”的工作主线,陆续推出了一批产业政策,这些政策对促进浦东新区产业加快发展发挥了积极作用。本课题通过对浦东新区经济现
在印度西部阿拉伯海漫长的海岸线上,拥有大量的封闭型海域和海湾。近几年来,这些水域受到了日益严重的原油污染的威胁。油污染一般来自(1)港口及油码头,(2)离岸油井,(3)油轮
随着我国经济的发展,社会主义市场体制日趋成熟,企业文化与思想政治建设情况在国有企业发展过程中占据越来越重要的作用.而二者的有机结合能最大效率的促进国有企业的发展,所
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
西太平洋北赤道逆流槽上部水域1 000m 以浅分布4个水团:北太平洋热带表层水、北太平洋次表层水、北太平洋中层水和南极太平洋中层水,它们的交界分别位于75、200和310m 深左右
现代化的社会发展步伐不断加快,很多地方的工作成绩拓展,都必须从长远的角度出发,不能继续按照简单的模式来操作.供电企业文化的品牌建设,已经成为了行业内高度关注的对象,在