Y(NO3)3 and NH3·H2O were used as a raw materials,and nano-Y2O3 powder was successfully synthesized by a precipitation method.Employing TEOS as a raw material,SiO2 powder was successfully prepared by a alkoxide-hydrolysis method,and a Y2O3/SiO2 composite powder was obtained by coating.The Y2O3,SiO2,and Y2O3/SiO2 powders were characterized using X-ray diffraction(XRD),scanning electron microscopy(SEM),and Fourier transform infrared spectrophotometer(FT-IR);the Y2O3 and Y2O3/SiO2 powders were further examined by photoluminescence(PL) spectra.The results indicated that the Y2O3 powder had a body-centered cubic structure with an average size of 35 nm,while the SiO2 powder was amorphous,with an average size of 145 nm and a narrow size distribution.The PL spectra of the Y2O3 and Y2O3/SiO2 powders showed that their wavelength of emission spectra were 585 nm,while their wavelength of excitation spectra were in the range of 240-260 nm.The optical properties of the Y2O3/SiO2 powder were identical to the Y2O3 powder.
Y (NO3) 3 and NH3 · H2O were used as a raw materials, and nano-Y2O3 powder was successfully synthesized by a precipitation method. Employing TEOS as a raw material, SiO2 powder was successfully prepared by a alkoxide-hydrolysis method, and a Y2O3, SiO2 and Y2O3 / SiO2 powders were characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), and Fourier transform infrared spectrophotometer (FT-IR) Y2O3 and Y2O3 / SiO2 powders were further examined by photoluminescence (PL) spectra. The results indicated that the Y2O3 powder had a body-centered cubic structure with an average size of 35 nm, while the SiO2 powder was amorphous, with an average size of 145 nm and a narrow size distribution. The PL spectra of the Y2O3 and Y2O3 / SiO2 powders showed that their wavelength of emission spectra were 585 nm, while their wavelength of the excitation spectra were in the range of 240-260 nm. The optical properties of the Y2O3 / SiO2 powder were identica l to the Y2O3 powder.