The process of electrodepositing Fe-Cr2O3 composite coating on polyacrylonitrile (PAN)-based carbon fibers and its catalytic graphitization were studied. Carbon
【机 构】
：
College of Chemistry and Chemical Engineering,State Key Laboratory of Chemo/Biosensing and Chemometr
论文部分内容阅读
The process of electrodepositing Fe-Cr2O3 composite coating on polyacrylonitrile (PAN)-based carbon fibers and its catalytic graphitization were studied. Carbon fibers with and without electrodeposited Fe-Cr2O3 composite coating were heat treated at different temperatures and the structural changes were characterized by XRD, Raman spectroscopy and SEM. The results indicate that Fe-Cr2O3 composite coating exhibits a significant catalytic effect on graphitization of carbon fibers at low temperatures. When the Fe-Cr2O3-coated carbon fibers were heat treated at 1 300 °C, the interlayer spacing (d002) and ratio of relative peak area (AD/AG) reach 3.364 - and 0.34, respectively. Whereas, the extent of graphitization of pristine carbon fibers is comparatively low even after heat treatment at 2 800 °C and the values of d002 and AD/AG are 3.414 - and 0.68, respectively. The extent of graphitization of carbon fibers increases not only with the increase of the catalyst gross but also the Cr2O3 content in Fe-Cr2O3 coating. The catalytic effect of Fe-Cr2O3 composite coating accords with the dissolution-precipitation mechanism.
其他文献
目的探讨不同栓塞材料在肝硬化合并脾功能亢进部分性脾栓塞术(PSE)中的临床应用。方法32例肝硬化并脾功能亢进患者行PSE治疗,根据栓塞材料的不同分为3组:A组12例,采用00000手
Four modified starches with selected charge characteristics including cationic starch (CAS), carboxymethyl starch (CMS), amphoteric starch (AMS) and soluble sta
Aluminum production by carbothermo-chlorination reduction of alumina in vacuum was investigated by XRD, SEM, EDS and thermodynamic analysis. Thermodynamic calcu
Eu-doped GaOOH nanoparticles with size of 5-8 nm were prepared by hydrothermal method using sodium dodecylbenzene sulfonate (SDBS) as surfactant. Eu-doped α-Ga
Citric acid was used to selectively extract cobalt from limonite-type laterite ores in the presence of ammonium bifluoride. The results show that ammonium biflu
A new model for describing the compaction process of iron powder was proposed based on the continuum hypothesis and elliptical yield criterion. To simulate the
A single specimen test using the three point single edge notched beam configuration at low temperatures for obtaining hot mix asphalt(HMA)resistance curves is d