The effects of Mg enhancement and heat treatment on the microstructures and tensile properties of Al_2Ca-added ADC12 die casting alloys were investigated. 0.3% and 0.5% Mg in the form of a master alloy including a trace amount of Al_2Ca were added to conventional ADC12(383 and AlSi10Cu2Fe) alloy with an initial Mg-content of 0.3% to increase the Mg content to 0.6% and 0.8%, respectively. To avoid heat treatmentinduced surface blisters, shortened solution treatment for 15 min at 490 ℃ and artificial aging for 6 h at 150 ℃ was undertaken. The results show that a 10% improvement in the shape factor of eutectic Si particles was achieved for Al_2Ca-added ADC12 with 0.8% Mg compared to the conventional ADC12 in the as-aged condition. Al_2Ca-added ADC12 with 0.8% Mg exhibited a yield strength of 289 MPa, a tensile strength of 407 MPa, and an elongation of 4.22%.
The effects of Mg enhancement and heat treatment on the microstructures and tensile properties of Al_2Ca-added ADC12 die casting alloys were investigated. 0.3% and 0.5% Mg in the form of a master alloy including a trace amount of Al_2Ca were added to conventional ADC12 ( 383 and AlSi10Cu2Fe) alloys with an initial Mg-content of 0.3% to increase the Mg content to 0.6% and 0.8%, respectively. To avoid heat treatment induced surface blisters, shortened solution treatment for 15 min at 490 ° C and artificial aging for 6 h at 150 ° C was undertaken. The results show that a 10% improvement in the shape factor of eutectic Si particles was achieved for Al_2Ca-added ADC12 with 0.8% Mg compared to the conventional ADC12 in the as-aged condition. 0.8% Mg exhibited a yield strength of 289 MPa, a tensile strength of 407 MPa, and an elongation of 4.22%.