Using the inexpensive inorganic salts as the starting materials,pure yttria nanopowders were prepared by sol-gel method. The primary particles are spherical and about 60 nm in diameter with a narrow size distribution. Moderate sulfate ions used as additive were the key to the formation of precursor and the preparation of spherical Y_2O_3 nanopowders. Transformation of the precursor was investigated during the calcining. The influence of calcination temperature on size and purity of production was analyzed. The results show that higher temperature is beneficial to the preparation of pure and complete crystallization of yttria powders under the condition of not making particles excessively grow.
Using the inexpensive inorganic salts as the starting materials, pure yttria nanopowders were prepared by sol-gel method. The primary particles are spherical and about 60 nm in diameter with a narrow size distribution. Moderate sulfate ions used as additive were the key to the formation of precursor and the preparation of spherical Y 2 O 3 nanopowders. Transformation of the precursor was investigated during the calcining. The influence of calcination temperature on size and purity of production was analyzed. The results show that higher temperature is beneficial to the preparation of pure and complete crystallization of yttria powders under the condition of not making particles excessively grow.