人们关注一种先进的(动态离子混合)复合工艺。这种高能量的工艺改善了复合物的粘结性能、结构控制及与沉积系统无关的相形成。法国学者用这种工艺在室温下沉积了均匀的1μm厚的TiB_2陶瓷。实际上,这种先进动态离子混合增加了薄膜和基体的粘结,诱发出一种六方晶系的相,它可以产生2200～2800kg/mm~2的硬度(一般沉积态的TiB_2薄膜是非晶的,而且不硬)。用该工艺制备的TiB_2相当的硬,并且惰性大,以至于对小批量
People are concerned about an advanced (dynamic ion mixing) composite process. This high-energy process improves the bond properties of the composite, structural control, and phase formation independent of the deposition system. French scholars have used this process to deposit a uniform 1 μm thick TiB 2 ceramic at room temperature. In fact, this advanced dynamic ion mixing increases the bond of the film to the substrate, inducing a hexagonal phase that produces a hardness of 2200 to 2800 kg / mm2 (generally the as-deposited TiB2 thin film is amorphous , But not hard). The TiB 2 produced by this process is quite hard and inert enough to be used in small lots