论文部分内容阅读
福建省漳平水泥厂采用高铁硅酸盐早强水泥熟料及其生产方法,成功地生产出道路水泥、填补了福建省水泥系列空白。1990年8月29～30日通过了鉴定。与会代表一致认为:提交审查的技术资料文件基本齐全正确,其特点是:铝氧率低,硅酸三钙和铁铝酸钙含量较高,不含或少含C_3A。性能特点:抗折强度高,28天龄期抗折强度比普通硅酸盐水泥高0.1～0.3MPa。早期强度发挥快:3天/28天,7天/28天的
Fujian Zhangping Cement Plant using high-speed early strength silicate cement clinker and its production methods, the successful production of road cement, cement to fill gaps in Fujian Province. August 1990 29 to 30 passed the appraisal. Delegates agreed that: submitted to review the basic technical documents are complete, characterized by: a low alumina, calcium silicate and calcium iron aluminate content is high, with or without C_3A. Features: High flexural strength, 28-day-old flexural strength higher than ordinary Portland cement 0.1 ~ 0.3MPa. Early strength to play fast: 3 days / 28 days, 7 days / 28 days