Positron lifetime spectra have been measured in binary Ni Al alloys with different chemical composition and NiAl alloys doped with Cr, Zr, Fe and Mg. The results indicate that in B2 NiAl and Ll 2 Ni 3Al alloys, some of the valance electrons of Ni and Al atoms are localized, which leads to a lower free electron density of the alloy. The mean free electron density of the binary Ni Al alloy decreases with increasing Al content. The open volume of defects on grain boundary of the Ni 3Al is larger than that of monovacancy or dislocation. Structural vacancies and microvoids are found in B2 NiAl alloys with Al content above 45%(mole fraction), and the concentration of the vacancies and open volume of microvoids will increase with higher Al content. The addition of Cr, Zr and Fe into a NiAl alloy can increase its mean free electron density and reduce the open volume of defects on its grain boundary, while with addition of Mg into the NiAl alloy, its mean free electron density decreases and open volume of boundary defects increases.
Positron lifetime spectra have been measured in binary Ni Al alloys with different chemical composition and NiAl alloys doped with Cr, Zr, Fe and Mg. The results indicate that in B2 NiAl and Li 2 Ni 3Al alloys, some of the valance electrons of Ni and The mean free electron density of the binary Ni Al alloy decreases with increasing Al content. The open volume of defects on grain boundary of the Ni 3Al is larger than that of monovacancy or dislocation. Structural vacancies and microvoids are found in B2 NiAl alloys with Al content above 45% (mole fraction), and the concentration of the vacancies and open volume of microvoids will increase with higher Al content. The addition of Cr, Zr and Fe into a NiAl alloy can increase its mean free electron density and reduce the open volume of defects on its grain boundary, while with addition of Mg into the NiAl alloy, and open volume of boundary defects increases.