In-situ observation of porosity formation during directional solidification of two Al-Si alloys (7%Si and 13%Si) was made by using of micro-focus X-ray imaging.In both alloys,small spherical pores initially form in the melt far away from the eutectic solid-liquid (S/L) interface and then grow and coagulate during solidification.Some pores can float and escape from the solidifying melt front at a relatively high velocity.At the end of solidification,the remaining pores maintain spherical morphology in the near eutectic alloy but become irregular in the hypoeutectic alloy.This is attributed to different solidification modes and aluminum dendrite interactions between the two alloys.The mechanism of the porosity formation is briefly discussed in this paper.
In-situ observation of porosity formation during directional solidification of two Al-Si alloys (7% Si and 13% Si) was made by using of micro-focus X-ray imaging.In both alloys, far away from the eutectic solid-liquid (S / L) interface and then grow and coagulate during solidification. The pores can escape from the solidifying melt at a relatively high velocity. At the end of solidification, the remaining pores maintain spherical morphology in the near eutectic alloy but become irregular in the hypoeutectic alloy.This is attributed to the different solidification modes and aluminum dendrite interactions between the two alloys. the mechanism of the porosity formation is briefly discussed in this paper.