The present work contributed to a new developed production method for enhancing the quality of isoamylene (IA) by adding a small amount of tertiary amyl alcohol (TAA) to the catalyst of strong acid cation exchange resin.TAA improved the selectivity of 2-methyl-2-butene (2M2B) at a high conversion level for the isomerization of IA.Compared with the other results from the current IA units,the conversion of 2-methyl-1-butene (2M1B),the mass ratio of 2M2B to 2M1B and the selectivity of 2M2B were increased from 0.5474,7.32 and 0.6864 to 0.72,12 and 0.95,respectively,while the dimers content in the products decreased from 4.38% to below 1.0%.Optimized conditions for IA isomerization consisted of temperature between 28 and 33°C and system pressure of 0.5 MPa,weight hourly space velocity of 8.0 h-1 with TAA mass fraction of 0.7%-0.9% in raw material.The results in lab supported bases for the developed process in industrial application which was later proved to be successful.In addition,a possible mechanism of the isomerization process was speculated to propose a key step of water formation in the TAA-added isomerization process and a verified experiment was conducted to support this speculation.
The present work contributed to a new developed production method for enhancing the quality of isoamylene (IA) by adding a small amount of tertiary amyl alcohol (TAA) to the catalyst of strong acid cation exchange resin. TAA improved the selectivity of 2-methyl- 2-butene (2M2B) at a high conversion level for the isomerization of IA.Compared with the other results from the current IA units, the conversion of 2-methyl-1- butene (2M1B), the mass ratio of 2M2B to 2M1B and the selectivity of 2M2B was increased from 0.5474, 7.32 and 0.6864 to 0.72, 12 and 0.95, respectively, while the dimers content in the decreased percentage from 4.38% to below 1.0%. Optimized conditions for IA were initially consisted of temperatures between 28 and 33 ° C and system pressure of 0.5 MPa, weight hourly space velocity of 8.0 h-1 with TAA mass fraction of 0.7% -0.9% in raw material. The results in lab supported bases for the developed process in industrial application which was later proved to be successful.In addition, a poss ible mechanism of the isomerization process was speculated to propose a key step of water formation in the TAA-added isomerization process and a verified experiment was conducted to support this speculation.