以NiAl-2.5Ta-7.5Cr-1B合金为研究对象,分析了合金在不同温度下的摩擦磨损性能。通过对试样在不同温度下摩擦系数、磨损体积损失、腐蚀产物微观组织形貌及成分的表征,揭示了
论文部分内容阅读
以NiAl-2.5Ta-7.5Cr-1B合金为研究对象,分析了合金在不同温度下的摩擦磨损性能。通过对试样在不同温度下摩擦系数、磨损体积损失、腐蚀产物微观组织形貌及成分的表征,揭示了不同温度对NiAl合金的磨损性能影响规律。结果表明,随着温度升高,合金表面形成陶瓷润滑膜,合金的耐磨性提高。
Taking NiAl-2.5Ta-7.5Cr-1B alloy as the research object, the friction and wear properties of the alloy at different temperatures were analyzed. The friction coefficient, wear volume loss, microstructure and corrosion resistance of the samples were characterized by different temperatures. The influence of different temperature on the wear properties of NiAl alloy was revealed. The results show that with the increase of temperature, a ceramic lubricating film is formed on the surface of the alloy, and the wear resistance of the alloy is improved.
其他文献
The effects of double shielded TIG(tungsten inert gas)torch’s structural parameters,including the flow rate ratio between the inner and outer layers of gas and
①形状复杂的易变形工件,可采用空气预冷或降温预冷后再淬入冷却剂。②轴类工件应垂直淬入冷却剂。③长板状工件应横向侧面淬入冷却剂。④套筒和薄壁圆环状工件,应沿轴向淬入
以美国超临界水堆(SCWR)设计为研究对象,开发超临界水堆的物理-热工耦合计算程序。该计算程序采用Dragon和Donjon直接耦合计算,提高计算精度和速度;并在功率迭代中引入松弛因
通过统计和ArcGIS分析发现:女性比例与经济发展速度正相关,即经济发展速度越高的年份,女性比例越高;经济发展速度越慢的年份,女性比例就越低,女性比列高低成为测度经济发展前
(2014年7月,青岛)主办单位:全国热处理学会协办单位:全国热处理标准化技术委员会;《材料热处理学报》编辑部;《金属热处理》杂志社;热处理学会冷却技术委员会;热处理学会化学
The tarnishing test in the presence of hydrogen sulfide(H_2S) vapors has been used to investigate the tarnish resistance capability of copper-based alloys coate
【本刊2014年2月综合报道】2013年,全球核电逐步走出日本福岛第一核电厂事故的阴影,并呈现出恢复增长的势头:美国正式启动了近30年来首批4台新核电机组的建设工作,俄罗斯政府
以全范围模拟机为平台模拟中国改进型百万千瓦级压水堆(CPR1000)堆型核电机组在发生单根传热管断裂事故(SGTR)瞬态,对事故后1.5 h不干预和1.5 h内依照事故规程进行干预分别进
研究了T23钢的热变形行为,并建立了材料的热加工图。结果表明,在热压缩过程中T23钢有动态再结晶及动态回复两种软化机制,随着减少变形速率或升高变形温度,动态再结晶产生的趋
以美国10 MW熔盐实验堆(MSRE)为研究对象,设计空气冷却和水冷却2种非能动余热排出系统。通过建立相应的数学模型,采用C++语言编程,分别对系统的主要特性进行研究,并对2种系统