The physical and electrical properties of lanthanum doped Pb(Zr,Ti)O_3 ceramic sheets(PLZT)which were prepared by tape casting method were carried out.Tape casting of lanthanum modified PZT was performed using commercial cellulose acetate binders and poly(ethylene glycol)plasticizers in ethanol solvent.Tapes from these slips were casted on a polymer substrate.The PLZT green tapes were stacked for 5 units and sintered in air at 1050℃ for 1 h with heating rate 5℃/min.SEM micrographs show that the tape is dense(90.26% of theoretical density)and rather uniform with grain size of approximately 1.1 ?m.The dielectric permittivity and loss tangent of PLZT ceramics as a function of temperature at 1 kHz suggest that the compounds exhibit a phase transition of diffuse type.The transition temperature(T_m)and piezoelectric coefficient(d_ 33)were 110℃ and 117 pC/N,respectively.
The physical and electrical properties of lanthanum doped Pb (Zr, Ti) O_3 ceramic sheets (PLZT) which were prepared by tape casting method were carried out. Tap casting of lanthanum modified PZT was performed using commercial cellulose acetate binders and poly (ethylene glycol) plasticizers in ethanol solvent.Tapes from these slips were casted on a polymer substrate. PLZT green tapes were stacked for 5 units and sintered in air at 1050 ° C for 1 h with heating rate 5 ° C / min. SEM micrographs show that the tape is dense (90.26% of theoretical density) and rather uniform with grain size of approximately 1.1? m. The dielectric permittivity and loss tangent of PLZT ceramics as a function of temperature at 1 kHz suggest that the compounds exhibit a phase transition of diffuse type. Transition temperature (T_m) and piezoelectric coefficient (d_33) were 110 ° C and 117 pC / N, respectively.