Spherical LiFePO4 and LiFePO4/C composite powders for lithium ion batteries were synthesized by a novel processing route of co-precipitation and subsequent calc
【机 构】
：
School of Materials Science and Engineering
论文部分内容阅读
Spherical LiFePO4 and LiFePO4/C composite powders for lithium ion batteries were synthesized by a novel processing route of co-precipitation and subsequent calcinations in a nitrogen and hydrogen atmosphere. The precursors of LiFePO4, LiFePO4/C composite and the resultant products were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), and the electrochemical performances were investigated by galvanostatic charge and discharge tests. The precursors composed of amorphous Fe3(PO4)2·xH2O and crystalline Li3PO4 obtained in the co-precipitation processing have a sphere-like morphology. The spherical LiFePO4 derived from the calcinations of the precursor at 700 ℃ for 10 h in a reduction atmosphere shows a discharge capacity of 119 mAh·g -1 at the C/10 rate, while the LiFePO4/C composite with 10wt.% carbon addition exhibits a discharge capacity of 140 mAh·g -1.The electrochemical performances indicate that the LiFePO4/C composite has a higher specific capacity and a more stable cycling performance than the bare olivine LiFePO4 due to the carbon addition enhancing the electronic conductivity.
其他文献
The UO2 ceramic microspheres are the most important materials in the spherical fuel elements for high temperature reactor (HTR). A process for preparation of UO
The weighted Poincaré inequalities in weighted Sobolev spaces are discussed,and the necessary and sufficient conditions for them to hold are given. That is, th
Static tensile test and tensile-tensile fatigue test of medium carbon steel sheet specimens with surface crack precut were performed on MTS810 hydraulic testing
In the search for improved materials for rechargeable lithium batteries, LiFePO4 offers interesting possibilities because of its low raw materials cost, environ
There have been several developments in determining the spontaneous combustion liability of coal. Most of the methods of concern have purely been based on the i
TiCoTi granular films were prepared by DC facing-target magnetron sputtering system onto glass substrates and subsequently in situ annealing in vacuum. Structur
Modified lithium manganese oxides were prepared by solid-state reaction of LiMn2O4 and LiCoO2 as raw materials. A study was carried out by TG-DSC,XRD, DSC and e
In this study, carbon aerogels were derived via the pyrolysis of resorcinol-formaldehyde (RF) aerogels, which were cost-effectively manufactured from RF wet gel
A novel sulfonated polyhedral oligomeric silsesquioxane(S-POSS) monomer was synthesized successfully in this article. S-POSS acted as a donor of sulfonic acid g
Based on the cermet double layer structure, Nb-NbN multi-layer films for solar selective coatings were deposited by direct current reactive magnetron sputtering