论文部分内容阅读
Surface coating of granular propellants is widely used in a multiplicity of propellants for small, medium and large caliber ammunition. All small caliber ball propellants exhibit burning progressivity due to application of effective deterrent coatings. Large perforated propellant grains have also begun utilizing plasticizing and impregnated deterrent coatings with the purpose of increasing charge weights for greater energy and velocity for the projectile. The deterrent coating and impregnation process utilizes volatile organic compounds(VOCs) and hazardous air pollutants(HAPs) which results in propellants that need to be forced air dried which impacts air quality. Propellants undergo temperature fluctuations during their life. Diffusion coefficients vary exponentially with variations in temperature. A small temperature increase can induce a faster migration, even over a short period of time, which can lead to large deviations in the concentration. This large concentration change in the ammunition becomes a safety or performance liability. The presence of both polymeric deterrents and nitroglycerin(NG) in the nitrocellulose matrix and organic solvents leads to higher diffusion rates. This results in continued emissions of VOCs and HAPs. Conventional polymers tend to partition within the propellant matrix. In other words,localized mixing can occur between the polymer and underlying propellant. This is due to solvent induced softening of the polymer vehicle over the propellant grain. In effect this creates a path where migration can occur. Since nitrate esters, like NG, are relatively small, it can exude to the surface and create a highly unstable and dangerous situation for the warfighter. Curable polymers do not suffer from this partitioning due to “melting” because no VOC solvents are present. They remain surface coated. The small scale characterization testing, such as closed bomb testing, small scale sensitivity, thermal stability,and chemical compatibility, will be presented. The 30 mm gun demonstration firing data at hot, cold, and ambient temperatures will also be presented.
Surface coating of granular propellants is widely used in a multiplicity of propellants for small, medium and large caliber ammunition. All small caliber ball propellants exhibit burning progressivity due to application of effective deterrent coatings. Large perforated propellant grains have also employed utilizing plasticizing and impregnated deterrent coatings with the purpose of increasing charge weights for greater energy and velocity for the projectile. The deterrent coating and impregnation process volatile volatile organic compounds (VOCs) and hazardous air pollutants (HAPs) which results in propellants that need to be forced air dried which impacts air mass. Propellants undergo temperature fluctuations during their life. A large temperature increase can induce a faster migration, even over a short period of time, which can lead to large deviations in the concentration. This large concentration change in the The results of both safety and performance liability. The presence of both polymeric deterrents and nitroglycerin (NG) in the nitrocellulose matrix and organic solvents leads to higher diffusion rates. This result in continued emissions of VOCs and HAPs. Conventional polymers tend to partition within the propellant matrix. In other words, localized mixing can occur between the polymer and the underlying propellant. This is due to solvent induced softening of the polymer vehicle over the propellant grain. , are relatively small, it can exude to the surface and create a highly unstable and dangerous situation for the warfighter. Curable polymers do not suffer from this partitioning due to “melting ” because no VOC solvents are present. They remain surface coated. The small scale characterization testing, such as closed bomb testing, small scale sensitivity, thermal stability, and chemical compatibility, will be presented. The 30 mm gun demonstration firing data at hot, cold, and ambient temperatures will also be presented.