【摘 要】
：
In order to improve the wear resistance of elastic metallic-plastic thrust bearing pad,micro-assembling PTFE/Al2O3 multi-layer film was developed by alternating
【机 构】
：
Department of Materials Science and Engineering
论文部分内容阅读
In order to improve the wear resistance of elastic metallic-plastic thrust bearing pad,micro-assembling PTFE/Al2O3 multi-layer film was developed by alternating radio frequency(RF)magnetron sputtering PTFE and Al2O3 targets.For enhancing the adhesion of the interfaces between PTFE and Al2O3 film,N+ implantation was employed.The structure,mechanical and micro-tribological properties were studied by XPS,X-ray photoelectron spectrometer and atomic force and friction force microscope(AFM/FFM).The results show that the multi-layer consists of Al2O3 component and crystalline PTFE.The hardness of the multi-layer modified by ion implantation is less than that of Al2O3,but its toughness is greatly improved.The friction coefficient of PTFE/ Al2 O3 multi-layer modified by ion implantation is much lower than that of Al2 O3 film,and its resistance to wear is much greater than that of PTFE film.Therefore the wear resistance of elastic metallic-plastic thrust bearing pad is greatly improved.
其他文献
利用弹性理论分析了稀土原子铈 (Ce)与 2 0 90铝锂合金中其它溶质原子 (Cu和 L i)间的交互作用 ,并采用离子探针和透射电镜 (TEM )分析研究了微量 Ce的添加对 Cu和 L i结合能
简要分析了硬质合金注射成形工艺各步骤中可能出现的各种缺陷及其产生的主要原因 ;讨论了减少或消除这些缺陷的有效措施 ;同时指出了硬质合金注射成形的应用前景及需解决的问
通过等温恒应变速率压缩实验，系统地研究了不同预处理、热力参数及分段变速变形对致密 ＦＧＨ９５合金高温变形特性的影响．研究结果表明，经热等静压致密的ＦＧＨ９５合金坯料，可以通过适当的预处理，以
以海绵钛为原料 ,源溶液经微波辐射 ,生成水合二氧化钛溶胶 ,加入少量无水乙醇 ,在 10 0℃以下 ,常压烘干 ,制备出纳米 Ti O2 粉末。 XRD分析纳米 Ti O2 粉末的晶体结构为锐
研究了结构陶瓷材料的统计分布规律.首先通过实验测试了两种Al2O3陶瓷光滑试件和不同缺口半径试件的断裂强度;对实验数据用正态分布和Weibull分布分别进行了分析,发现对于缺
研究了电磁搅拌对半固态 ＡｌＳｉ７Ｍｇ合金连铸坯料组织的影响．研究结果表明：电磁搅拌功率是重要的影响因素，搅拌功率越大，球状的初生α－Ａｌ端部形态越圆整，蔷薇状的初生α－Ａｌ越少、尺寸越小，连铸坯表
测量了一系列不同隔离层(spacer)厚度、阱宽和硅δ掺杂浓度的单边掺杂的赝形高电子迁移率晶体管(p-HEMTs)量子阱的变温和变激发功率光致发光谱,详细研究了(el-hh1)和(e2-hh1)
The three-dimensional solidification simulation of the investment castings of single crystal hollow turbine blade at the withdrawal rates of 2 mm/min, 4.5 mm/mi
The erosion behavior of Kapton when exposed to atomic oxygen (AO) environment in the ground-based simulation facility was studied. The chemical and physical cha
当前我国经济形势发展良好，各个领域的工程建设都在如火如荼地开展着，尤其是公路工程的里程数不断地扩大，在拉动我国城市化进程速度上发挥着不可获取的作用。公路工程施工中最重