【摘 要】
：
熔体过热度对Cu36Zr48Ag8Al8块体非晶合金的热稳定性和力学行为有显著影响。高的过热水平制备非晶合金的比热容大,初始缺陷密度小,热稳定性高。过热度越小,压缩塑性越小;抗压
【机 构】
：
兰州理工大学甘肃省有色金属新材料省部共建国家重点实验室,北京工业大学国家教育部功能材料重点实验室,
论文部分内容阅读
熔体过热度对Cu36Zr48Ag8Al8块体非晶合金的热稳定性和力学行为有显著影响。高的过热水平制备非晶合金的比热容大,初始缺陷密度小,热稳定性高。过热度越小,压缩塑性越小;抗压强度和维氏硬度随着过热度的减小先增加后下降。自由体积和残余应力共同影响不同吸铸电压制得非晶合金的力学性能。
The degree of superheat of the melt has a significant effect on the thermal stability and mechanical behavior of the Cu36Zr48Ag8Al8 bulk amorphous alloy. The high specific heat capacity of amorphous alloy prepared by high level of overheating is large, the initial defect density is small, and the thermal stability is high. The lower the degree of superheat, the smaller the plasticity of compression; the compressive strength and Vickers hardness increase first and then decrease with the decrease of superheat degree. Free volume and residual stress together affect the mechanical properties of amorphous alloys prepared by different casting voltage.
其他文献
采用模拟体液浸泡法评价碱液处理TLM(Ti-25Nb-3Zr-2Sn-3Mo)合金的生物活性.钛合金TLM经过碱液处理后表面生成了钛(铌)酸钠凝胶层,凝胶层厚度随碱液浓度升高而增加.在模拟体液
采用强度测试、SEM、HRTEM等分析测试手段对纤维表面去碳前后SiC纤维强度、复合材料力学性能、纤维表面形貌、复合材料断口形貌以及复合材料界面特征进行分析表征。结果表明,
使用CaCO3和CaHPO4混合粉末,在纯钛表面通过激光熔覆原位合成的方法制备羟基磷灰石(Ca10(PO4)6(OH)2,HA)涂层,研究了激光功率,扫描速度和热处理对涂层物相的影响,以期提高涂
采用化学抛光处理钛、阳极氧化和微弧氧化处理钛作为生物材料模型，研究成骨细胞 MG-63在其表面的黏附和增殖机理。结果表明，阳极氧化和微弧氧化处理的钛表面通过促进 MG-63细胞
提出了一种多区间主成分交互验证法.该方法根据目标气体的光谱特征吸收峰,在全光谱范围内划分出多个特征波数区间,同时,对单组分气体构成的参考光谱矩阵在划分出的特征波数区
通过直流平衡磁控溅射法在NiTi SMA表面生成Zr-Ti膜,用SEM、XRD和XPS分析证实制各的Zr-Ti膜呈现晶带T型结构,组织保持了细小致密的纤维状特征,与基底结合良好,并且出现了少量
The aim of this study is to investigate the change of mechanical properties of human dentin due to aging and spatial variation. Sections of coronal dentin are m
比较研究了Mg-(RE)-Zn合金铸态和经560℃扩散退火后的显微组织、物相及性能,发现铸态的Mg-(RE)-Zn合金经560℃保温7h扩散退火,原晶界区的共晶组织消失,晶界净化,材料成分和显
贵金属作为车用三效催化剂的主要催化活性组分,在净化汽车排放废气中发挥着重要作用。然而,贵金属在其前体化合物,即前驱体中的价态、贵金属与配体的键合强度、吸附在负载材
研究了烧结温度对 La0.6Ca0.4MnO3的结构、磁转变和磁熵的影响。观察表明，该化合物属于具有 Pnma空间群的斜方晶系结构，不含任何杂质。研究烧结温度对居里温度(TC)的影响，发现提