The melt-spun Nd8Fe85Nb1B6 ribbon was prepared by the single roller method with the tangential speed of 20 m/s. A mixture of Nd2Fe14B and α-Fe phases with the average crystalline grain size of about 20 nm was found to exist in the as-quenched ribbons. The