研究一种新型高强度冷轧薄板钢,其主要成分(wt.%)为:0.04C、0.2Si、1.5Mn、0.2P,钢锭先经锻造和热轧后冷轧成0.8mm薄板。结果表明:冷轧薄板经700退火后的机械性能为:σ_S=420
【机 构】
：
天津大学rrrrrrrrn,天津大学rrrrrrrrn,天津大学rrrrrrrrn,天津大学rrrrrrrrn,天津大学rr
论文部分内容阅读
研究一种新型高强度冷轧薄板钢,其主要成分(wt.%)为:0.04C、0.2Si、1.5Mn、0.2P,钢锭先经锻造和热轧后冷轧成0.8mm薄板。结果表明:冷轧薄板经700退火后的机械性能为:σ_S=420MPa,σ_b=530MPa,ε=31%,γ_m=1.5。经用x射线分析法测定退火前后织构的变化,以及用TEM观测Fe_3P相的析出后提出磷的偏聚和Fe_3P的弥散分布是影响织构发展的重要因素。
A new type of high strength cold rolled steel with a main component (wt.%) Of 0.04C, 0.2Si, 1.5Mn and 0.2P was studied. The ingot was first forged and then rolled into a 0.8mm sheet by hot rolling. The results show that the mechanical properties of the cold rolled sheet annealed at 700 are: σ_S = 420MPa, σ_b = 530MPa, ε = 31% and γ_m = 1.5. The change of texture before and after annealing was measured by x-ray analysis, and the segregation of phosphorus and the dispersion of Fe_3P after the precipitation of Fe_3P phase were observed by TEM are the important factors affecting the texture development.
其他文献
中国太阳能学会第四届理事长朱亚杰院士生平简介中国共产党党员，中国民主同盟盟员，中国科学院院士，第三届全国人大代表，全国政协第六、七届委员，中国太阳能学会理事长，中国石油学会
由我国著名世界经济学家滕维藻教授主编的涉外经济丛书《走向国际市场》１９９７年已由贵州人民出版社出版。这套大型丛书共出版了８本系列专著，１８０万字。著名经济学家马洪为之作序。这套丛
学习周鑫全 把海关精神文明建设推向前进本刊评论员今年以来，珠海市委、市政府，广东省口岸办，海关总署分别作出了关于开展向周鑫全同志学习的决定。伴随轰轰烈烈的学习活动，周鑫
今天是一个靠科技、知识和智能创业的时代，《黑龙江·科技信息》会助你在知识经济时代一跃而成为中国第四代富翁！篇篇是发财高招纵览世界最新科技经济信息页页是商海秘诀讲述天
通过实验建立了以高锰酸钾-磷钒钼黄法测定循环冷却水总磷的方法。该法与ZBG76002-90行业标准测定的结果无显著性差异,但该法具有操作简便、快速、易消除干扰等特点。该法标
2010年5月21日,由中国音乐家协会二胡学会、中国民族管弦乐学会二胡学会主办的罗兰电声二胡效果器全国首发会在北京朝阳公园郡王府举行,天津音乐学院副院长靳学东、中国音协
在“列二元一次方程组解应用题”时，发现有的同学能设适当的未知数，并且也列对了方程组，却仍然丢了分，原因是没有正确地解二元一次方程组，不同的方程组都有着各自巧妙的解法，同一个方程组也有着不同的解法.下面，我们以一道方程组的求解题为例，探索二元一次方程组的不同解法. 探究内容： （一） 用“常规解法”——“代入消元法”“加减消元法”解方程组； （二） 用“整体思想”解方程组； （三） 用“参数
[试题展示] 阅读下面的材料，根据要求写一篇不少于800字的文章。 想赢不怕输。每个人都想赢、不怕输，才是人生成功的关键。然而在生活中，你真的输什么都不怕么？ 要求：①角度自选；②立意自定；③题目自拟；④除诗歌外，文体自选。 [设计意图] 1.着力引导学生进行思辨式思考与表述。这是一则以“输”与“赢”的关系为话题的材料作文，“不怕输”是关键，强调“输”对于赢的积极的促进作用，“输什么都不