The Co3 Ti phase hardens appreciably by the fine precipitation of disordered fcc Co-rich phase upon aging after quenching from solution annealing temperature. Transmission electron microscope (TEM)observations revealed that the precipitates are platelet in shape, lying nearly parallel to the {100} planes of the L12-ordered matrix, and perfectly coherent with the matrix lattice at the beginning of aging. The high temperature strength increases appreciably with the fine precipitation of disondered Co-rich phase over the whole temperature range investigated. TEM observations of the deformed alloys after underaging revealed that saperdislocations are pinned by precipitates indicating an attractive interaction between dislocations and precipitates.
The Co3 Ti phase hardens appreciably by the fine precipitation of disordered fcc Co-rich phase upon aging after quenching from solution annealing temperature. Transmission electron microscope (TEM) observations showed that the precipitates are platelet in shape, lying nearly parallel to the {100} planes of the L12-ordered matrix, and perfectly coherent with the matrix lattice at the beginning of aging. The high temperature strength increases appreciably with the fine precipitation of disondered Co-rich phase over the whole temperature range investigated. TEM observations of the deformed alloys after underaging revealed that saperdislocations are pinned by precipitates indicating an attractive interaction between dislocations and precipitates.