【摘 要】
：
采用自孕育法制备6061变形铝合金半固态浆料,研究了浇注温度对自孕育法制备6061变形铝合金半固态浆料的影响。结果表明,随着浇注温度的降低,组织中的树枝晶逐渐减少,甚至消失
【机 构】
：
兰州理工大学省部共建有色金属先进加工与再利用国家重点实验室,兰州理工大学有色金属合金省部共建教育部重点实验室,
论文部分内容阅读
采用自孕育法制备6061变形铝合金半固态浆料,研究了浇注温度对自孕育法制备6061变形铝合金半固态浆料的影响。结果表明,随着浇注温度的降低,组织中的树枝晶逐渐减少,甚至消失,且存在大量均匀细小的近球状晶或蔷薇状晶。适合6061变形铝合金的温度加工区间为710~730℃,平均晶粒尺寸为32.3~36.2μm。与传统铸造相比,通过自孕育法能够获得均匀细小的半固态浆料组织。
The 6061 deformed aluminum alloy semi-solid slurry was prepared by self-inoculation method and the effect of pouring temperature on 6061 deformed aluminum alloy semi-solid slurry was studied. The results showed that with the decrease of pouring temperature, the dendrites in the tissue gradually decreased or even disappeared, and there were a large number of uniform and fine near-spherical crystals or rose-like crystals. Suitable for 6061 deformed aluminum temperature processing range of 710 ~ 730 ℃, the average grain size of 32.3 ~ 36.2μm. Compared with the traditional casting, by self-fertilization method can be uniform and small semi-solid slurry organization.
其他文献
采用正交试验、光学金相显微镜、透射电镜、能谱分析、X射线衍射、拉伸试验及电导率检测等手段,研究了时效处理温度和保温时间对挤压Al-Mg-Si合金组织及性能的影响。结果表明
制备了一种含Er和Zr元素的板材用Al-Mg-Si合金,其化学成分为Al-0.8Mg-1.0Si-0.8Cu-0.2Mn-0.15Zr-0.3Er。通过透射电镜、X射线衍射、扫描电镜、能谱和光学显微镜等分析,研究了
蔬菜喷施食醋,可提高光能利用率,增加产量,改善品质。茄果类蔬菜从定植后1～2天开始喷施,连喷3～5次300倍液的食醋,对防治病毒病有较好的效果,且可使番茄增产10%～34%,辣
Vinegar
采用数值模拟研究了40Cr钢奥氏体热变形行为。通过JMatPro软件得到本构关系曲线,建立了动态再结晶模型。在Deform-3D平台上将动态再结晶模型和元胞自动机模型结合起来,对40Cr
1.改善生态环境栽培场地要靠近水源、空气流畅、四周宽阔,远离禽畜饲养场、酿造厂、生活区及医院至少300米;场地采取翻土、晒白、灌水等措施取代农药进行消毒;水源水质清净无
新疆生产建设兵团农八师屯垦于新疆石河子市,地处天山北坡经济带的中心地段,是兵团迎接西部大开发的重要窗口。农八师是新疆重要的产棉区,引进和装备了采棉机32台,激光平地机
采用石墨型-砂型复合铸造工艺制作纯铜冷却壁,利用MAGMA软件模拟了该工艺下纯铜冷却壁的凝固过程,包括建立模型、网格划分、参数设置、模拟结果分析等。结果表明,冷却壁遵循
采用超声振动制备了Mg-6Zn-3RE-1.4Y新型镁合金的半固态浆料,并对半固态浆料进行直接挤压铸造。研究了流变挤压铸造Mg-6Zn-3RE-1.4Y镁合金的组织和相组成。结果表明,Mg-6Zn-3
采用石墨质蛇形通道浇注法制备半固态A380铝合金浆料,研究了浇注温度、弯道数量和弯道内径对半固态A380铝合金浆料组织的影响。结果表明,浇注温度在610~650℃范围时可获得理
农业作为全国第一大产业,其发展对于国家经济具有重大影响,而随着国家科学技术的快速发展,一些新的技术也在农业生产中得到了应用,如何加快农业技术推广成为了一个重大难题,