Mesoporous silica nanoparticles (MSN),with higher water permeability than NaA zeolite,were used to fabricate thin-film nanocomposite (TFN) reverse osmosis (RO) membranes.However,only aminoalkyl-modified MSN and low-pressure (less than 2.1 MPa) RO membrane were investigated.In this study,aminophenyl-modified MSN (AMSN) were synthesized and used to fabricate high-pressure (5.52 MPa) RO membranes.With the increasing of AMSN dosage,the crosslinking degree of the aromatic polyamide decreased,while the hydrophilicity of the membranes increased.The membrane morphology was maintained to show a ridge-and-valley structure,with only a slight increase in membrane surface roughness.At the optimum conditions (AMSN dosage of 0.25 g/L),when compared with the pure polyamide RO membrane,the water flux of the TFN RO membrane (55.67 L/ m2/h) was increased by about 21.6％,while NaCl rejection (98.97％) was slightly decreased by only 0.29％.However,the water flux of the membranes was much lower than expected.We considered that the enhancement of RO membrane permeability is attributed to the reduction of the effective thickness of the PA layer.