Microstructural evolution during reheating of A356 machining chips at semisolid state

• 作 者: Fang Wang Wen-qiang Zhang Wen-
• 机 构: KeyLaboratoryofAerospaceAdvancedMaterialsandPerformanceoftheMinistryofEducation,CenterforAdvancedDie
• 出 处: 矿物冶金与材料学报：英文版
• 发表日期: 2017年8期
• 关键词: SEMISOLID slurry aluminum CHIPS MICROSTRUCTURAL evolution grain COARSENING MICRO
• 基金项目: This work was financially supported by the InternationalScience and Technology Cooperation Program of China (No.2015DFA51430), the National Natural Science Foundationof China (No. 51401010), and the A

The microstructural evolution of A356 machining chips in the semisolid state was studied at different temperatures and holding times. The results showed that the elongated α-Al grains first recrystallized in the semisolid state and then became globular wi