In this work, the mechanical properties and microstructures of vermicular graphite cast iron processed by selective laser surface alloying with ultra-fine ZrO_2 ceramic particulates were investigated. A particulate-reinforced metal matrix composite coating with the thickness of ~650 μm was fabricated by laser treatment on the sample surface. The particulates were uniformly distributed in the microstructure of the coating. The tensile strength and microhardness both increased with the particulate fraction, since more tensile load was transferred from the matrix to the reinforcement showing essential strengthening effect. The composite coating also sharply reduced the wear mass loss and thus improved the wear resistance.
In this work, the mechanical properties and microstructures of vermicular graphite cast iron processed by selective laser surface alloying with ultra-fine ZrO 2 ceramic particulates were investigated. A particulate-reinforced metal matrix composite coating with the thickness of ~ 650 μm was fabricated by laser treatment The particulates were uniformly distributed in the microstructure of the coating. The tensile strength and microhardness both increased with the particulate fraction, since more tensile load was transferred from the matrix to the reinforcement show essential strengthening effect. The composite coating also sharply reduced the wear mass loss and thus improved the wear resistance.