【摘 要】
：
(AlTa0.76)xCoCrFeNi2.1 (x values in molar ratio,x =0.1,0.3,0.5,0.7,1.0,and 1.5) alloys were designed to investigate the microstructure and mechanical properties
【机 构】
：
Department of Nanotechnology and Advanced Materials Engineering,Sejong University,209 Neungdong-ro,G
论文部分内容阅读
(AlTa0.76)xCoCrFeNi2.1 (x values in molar ratio,x =0.1,0.3,0.5,0.7,1.0,and 1.5) alloys were designed to investigate the microstructure and mechanical properties of the eutectic high entropy alloys (EHEAs)consisting of FCC,B2,and Laves phases.Depending on the compositional variatio,clear microstructural variation was observed,as follows:(1) Group 1 :FCC dendrite + Laves interdendrite (x =0.1),(2) Group 2:FCC dendrite + fine-eutectic structure consisting of FCC and Laves phases (x =0.3,0.5 and 0.7),(3) Group 3:B2 dendrite + bimodal eutectic structure[FCC/B2 +Laves](x =1.0),(4) Group 4:Laves dendrite + eutectic structure consisting of B2 and Laves phases (x =1.5).As the fraction of Laves or B2 phases increases,yield stress increases from 293 to 2336 MPa,while the plastic strain decreases from 50 ％ to 2％.Thermo-physical parameters,such as mixing entropy (△Smix),mixing enthalpy (△Hmix),valence electron concentration(VEC),and atomic size difference (δr),were calculated to understand the microstructural variation.Two criteria (δr-VEC and δr-△Hmix) were utilized to elucidate the formation of the eutectic structures in the present EHEAs,revealing the usefulness of the thermo-physical parameters in the development of EHEAs.
其他文献
This work focused on the role of Al2O3 particles in the corrosion behavior of cold sprayed AA5083 alu-minum alloy matrix composite (Al-MMC) coatings.The electro
In additive manufacturing (AM),numerous thermal cycles make stress relaxation a significant factor in affecting the material mechanical response.However,the tra
The effects of cold work produced by peening processes in residual stress relaxation under elevated tem-peratures were investigated.Two types of peening process
A transparent energy storage device is an essential component for transparent electronics.The increasing demand for high-power devices stimulates the developmen
The low dielectric loss of mesoporous carbon hollow microsphere (PCHM) requires high filler loading(higher than 20 wt％) when it is used as microwave absorbers.In
Recently,high-and medium-entropy alloys (HEAs and MEAs) have been found to exhibit excellent cryo-genic mechanical properties,but most of them contain high-pric
Magnesium alloys are promising as load bearing components.They are inevitably exposed to cyclic load-ing and corrosive environment in actual service,which can c
The so-called 'negative difference effect'(NDE) was often defined by the increasing rate of hydrogen evo-lution from magnesium (Mg) surface under anodic polariz
Recently it is a hot topic to make full use of high abundant Y element in Nd2Fe14B-type permanent mag-nets.In contrast to Pr and Nd elements,Y shows different m