【摘 要】
：
我厂生产的C5523大立车往往因立柱导轨产生气孔而报废,通过分析导轨产生气孔的原因,我们采取了相应的措施,消除了气孔,保证了铸件质量,具体方法如下:一、铸件的特点及气孔产
论文部分内容阅读
我厂生产的C5523大立车往往因立柱导轨产生气孔而报废,通过分析导轨产生气孔的原因,我们采取了相应的措施,消除了气孔,保证了铸件质量,具体方法如下:一、铸件的特点及气孔产生的部位铸件形状见图1,材质为HT 20-40,轮廓尺寸3000×1200×1100mm,导轨壁厚处200mm,薄壁处25mm。铸件较大,厚薄不均,要求在保证导
I plant the C5523 Dali car often due to column stomatal obsolescence, through the analysis of the causes of stomatal guide, we have taken appropriate measures to eliminate the pores to ensure the quality of the casting, the specific methods are as follows: First, the characteristics of the casting Figure 1 shows the shape of the castings produced by the blowhole. The material is HT 20-40, the outline size is 3000 × 1200 × 1100mm, the thickness of the guide rail is 200mm, and the thickness is 25mm. Larger castings, uneven thickness, required to ensure the guide
其他文献
采用含～10at.-％B的Fe基多元合金,通过液态急冷及粉末冶金工艺可得到具有亚微米以下微晶组织的块状材料,这是一种正在开发中的新型材料,对其工艺过程中显微组织的变化特别是硼
甘肃北山地区位于甘肃省西北隅,是指疏勒河隐伏断裂以北,黑河以西至甘、新两省(区)交界处的广大地带,面积约六万多平方公里,属戈壁丘陵地貌区。据有关气象资料,本区属温带干
我厂生产的 ZZD-16-1型和 ZZD-22-1型电动倾翻渣缸车各有一个大型零件——支框,支框的形状相似,在长度方向的两端都有360mm 的孔,孔内都有宽80mm 的键槽,形状尺寸见下表:
T
使用图示工具在普通车床上,可加工 M16以下螺纹,莫氏锥柄的套筒8安装在车床尾座上,内滑套6的安装孔,选用过渡配合,由顶丝1将板牙固定。内滑套6加工一斜孔4,使冷却液流入板牙
井式保护气氛炉有个致命的弱点,就是工件出炉的氧化,特别是对表面质量要求较高的产品问题更为突击。为了克服这一难题,我们在吊具下作了改进,取得了很好的效果,同时在滴液及
藁城市在创建“三讲”文明机关活动中,站在全局的高度,不断向纵深发展,他们在办实事、解决问题上作文章,侧重为经济建设创造有利条件,取得了初步成效。建设优美环境,树立藁
在材料性能试验中,获得分段光滑曲线的连接点为不光滑点,这些不光滑点的某一个座标值所代表的物理量就是该材料的物性参数或叫材料常数,根据数学上分段光滑曲线定义知,在不光
加工铸铁的Widlanit切削材料主要由氮化硅(Si_3N_4)组成。它兼有硬质合金的韧性和氧化物陶瓷材料的热硬性。在加工铸铁时(图),切削速度可超过1000米/分。粗铣时,尽管出现微
Qingdao is well on its way to claiming the title of Sailing City in the post-Olympic era“Good morning and welcome aboard!” On a Friday morning in September, J
在美国经济非常不景气,以及明年预估将有不少王牌级的球员将成为自由球员的双重条件下,对今年成为自由球员的NBA球员来说,这可不是一个很美好的夏天……
This is not a very