【摘 要】
：
采用扫描电镜测试、金相检验、硬度测试、化学成分分析等方法对某型号重载工程车转向臂下端轴的断裂原因进行了分析。结果表明:该轴的断裂属于疲劳断裂,轴肩过渡处圆角未达到
【机 构】
：
国家标准件产品质量监督检验中心,中达建设集团股份有限公司,
论文部分内容阅读
采用扫描电镜测试、金相检验、硬度测试、化学成分分析等方法对某型号重载工程车转向臂下端轴的断裂原因进行了分析。结果表明:该轴的断裂属于疲劳断裂,轴肩过渡处圆角未达到设计要求以及机加工刀痕、冶金缺陷引起该位置应力集中是导致其疲劳断裂的主要原因。
The reason of the fracture of the lower arm of the steering arm of a heavy duty truck was analyzed by scanning electron microscopy, metallographic examination, hardness test and chemical composition analysis. The results show that the fracture of the shaft belongs to the fatigue fracture, the fillet of the shoulder transition does not meet the design requirements and machining marks, and the stress concentration in the position caused by the metallurgical defect is the main reason of the fatigue fracture.
其他文献
To acquire the engineering data of irradiation performance of the lithium ceramic breeder pebbles such as tritium release behaviors,retention characteristics an
国务院日前印发《全民健身计划(2016~2020年)》(以下简称《计划》),就今后一个时期深化体育改革、发展群众体育、倡导全民健身新时尚、推进健康中国建设作出部署。《计划》指
剪切系统是乏燃料后处理流程中首端处理的重要设备,目的是将乏燃料元件剪切成合适长度的短段,便于对短段进行溶解,实现芯块与包壳的分离。核燃料后处理放化实验设施的剪切系
The dedicated X80base metal,welding metal and X80/X02HAZ metal are irradiated in experimental reactor in order to evaluate the mechanical properties on the spec
一、前言随着体测改革的进行,学校作为连接社会的桥梁、人才培养的摇篮,在群众体育的后备力量的储备上也同样发挥着不可或缺的作用。学校体育是学生终身体育的基础,运动兴趣
乏燃料后处理工艺热实验是新流程投入中试之前的必要环节,为配合先进无盐二循环工艺热实验的开展,在核燃料后处理放化实验设施开展了相关分析实验设备及方法的安装调试。工艺
文玩玉石的收藏正呈现出百花齐放的态势,在和田玉、翡翠价格被推至令人咂舌的高位后,南红玛瑙正成为投资者的新晋热宠。南红玛瑙摩氏硬度为6.5左右,与和田玉(Hm=6-6.5)、翡翠
对于核燃料组件无损检测系统,入堆辐照后的燃料组件会辐射出大量的光子,对数据采集和图像重建产生严重的干扰。因此,需在燃料组件无损检测系统设计时,充分考虑其自身辐射的影
In order to provide a high pure sodium environment for properties testing in the fuel research for fast reactor,it is essential to fill sodium into fuel testing
核燃料后处理放化实验设施(CARAL)是我国重要的乏燃料后处理热试验平台。后处理实验产生的高放废液在暂存过程中会发生辐解产生氢气。适时精确测量贮槽上部空气的氢气浓度,是