Nanosized ZrO 2 powder was prepared by evaporative decomposition of solution(EDS).The particle size is from 50 nm to 200 nm.This process has such advantages as high purity,precise compositional control,simple procedure and successive auto-operating.In this process,mixed solution of zirconium acetate and yttrium nitrate was atomized to from a fine mist and blown into the hot zone from the bottom of furnace. The solution was rapidly decomposed at 900℃and the powder was collected by a filter system.The powder characteristics can be controlled by adjusting the concentration,droplet volume and decomposition temperature of the solution.
Nanosized ZrO 2 powder was prepared by evaporative decomposition of solution (EDS). The particle size is from 50 nm to 200 nm. This process has such advantages as high purity, precise compositional control, simple procedure and successively auto-operating. In this process , mixed solution of zirconium acetate and yttrium nitrate was atomized to from a fine mist and blown into the hot zone from the bottom of furnace. The solution was rapidly decomposed at 900 ° C and the powder was collected by a filter system. be controlled by adjusting the concentration, droplet volume and decomposition temperature of the solution.