Monosize, 1.6 μm, magnetic beads of poly(glycidyl methacrylate) [M-poly(GMA)], were prepared by dispersion polymerization in the presence of Fe3O4 nano-powder.
【机 构】
：
Department of Chemistry
论文部分内容阅读
Monosize, 1.6 μm, magnetic beads of poly(glycidyl methacrylate) [M-poly(GMA)], were prepared by dispersion polymerization in the presence of Fe3O4 nano-powder. Monosize M-poly(GMA) beads were characterized by swelling tests, density measurements, electron spin resonance (ESR), vibrating sample magnetometer (VSM) and scanning electron microscopy (SEM). The characteristic functional groups of M-poly(GMA)beads were analyzed by Fourier transform infrared spectrometer (FTIR). The M-poly(GMA) beads are highly uniform in size and have a spherical shape and non-porous structure. Polydispersity index (PDI) of M-poly(GMA) beads was calculated to be around 1.008. The hydrated density of the M-poly(GMA) beads measured at 25 ℃ was 1.14 g/cm3. The content of oxirane groups on the surface of the M-poly(GMA) sample was found to be 3.46 mmol/g by using perchloric acid titration. The specific surface area of the M-poly(GMA) beads was determined to be 3.2 m2/g.The equilibrium swelling ratio was 52%. The volume fraction of magnetite nanopowder in the M-poly(GMA) beads was found to be 4.5%. The g factor, that can be considered as a quantity characteristic of the molecules in which the unpaired electrons are located, was found to be 2.28for M-poly(GMA). The external magnetic field at resonance was calculated to be 2055 Gs which was found sufficient to excite all of the dipole moments present in 1.0 g of M-poly(GMA) sample.
其他文献
The title compound,[Cu2(CH3COO)4(C8H10N2)]n·nCH3CN1 (C8H10N2,4,4'-bipy = 4,4'-bipyridine),has been solvothermally synthesized in CH3CN and characterized by X-r
Sn-aniline complex was prepared by a simple procedure. Cyclic and acyclic ketones were oxidized into lactones or esters with very high selectivity and yield wit
This paper presents a performance-based methodology for the assessment of seismic vulnerability and capacity of buildings. The vulnerability assessment methodol
Single crystals of head-to-tail poly(3-hexylthiophene)s have been grown through the method of isothermal solution crystallization. Electron diffraction in combi
The effect of vanadium addition to Cu/γ-Al2O3 catalyst used in the hydrogenation of CO2 to produce methanol was studied. It was found that the catalytic perfor
Polymer layers adsorbed to a surface or in a confined environment often change their mechanical properties. There is even the possibility of solidification of t
As a part of the ongoing search for new constituents of Stemona species in China, chemical investigation of Stemona sessilifolia, a plant used in the traditiona
Hydrodynamic characteristics for two-dimensional flow around a waving plate are investigated. Under large Reynolds number approximation, the flow is assumed to
In this article, the authors consider equation ut = div(ψ(Гu)A(|Du|2)Du) -(u- I), where ψ is strictly positive and Г is a known vector-valued mapping, A: R+
为探究吕家坨井田地质构造格局,根据钻孔勘探资料,采用分形理论和趋势面分析方法,研究了井田7