【摘 要】
：
The effect of cryorolling on the precipitation process of deformed Cu-Ni-Si alloys was investigated through in situ synchrotron X-ray diffraction technique.The results demonstrate that the precipitation process is significantly accelerated by cryorolling.
【机 构】
：
Key Laboratory of Solidification Control and Digital Preparation Technology(Liaoning Province), Scho
论文部分内容阅读
The effect of cryorolling on the precipitation process of deformed Cu-Ni-Si alloys was investigated through in situ synchrotron X-ray diffraction technique.The results demonstrate that the precipitation process is significantly accelerated by cryorolling.Cryorolling produces higher dislocation density,which provides more heterogeneous nucleation sites for Ni2Si precipitates,hence promotes precipitation.In the early stage of aging,the enhanced nucleation of precipitates accelerates the depletion of supersaturation,and finer precipitates are obtained.In addition,recrystallization is promoted as a result of high stored energy in the cryorolled Cu-Ni-Si alloys,which facilitates the formation of discontinuous precipitation in the late stage of aging.
其他文献
Degradation behaviors of three typical La-Mg-Ni alloys,La2MgNi9,La1.5Mg0.5Ni7 and La4MgNi19,were studied.La1.5Mg0.5Ni7 with (La,Mg)2Ni7 as main phase presents better discharge capacity and cycling stability.The three alloys suffer severe pulverization and
Homogenization of physical properties and the chemical composition through the control of liquid metal flow is essential during the continuous casting production of billets.This work was aimed at obtaining improved finished products via continuous casting
In the present work,a CuCrZr alloy characterized by ultrafine grains and nanoscale particles was prepared by equalchannel angular pressing (ECAP) at 450 C.A desired combination of a tensile strength (580 MPa) and an electrical conductivity (81％ Internatio
The microstructure and stress-rupture property of the large-scale complex single crystal (SX) casting DD10 were investigated in high-rate solidification process.It is found that the primary dendrite arm spacing (PDAS) does not increase monotonically with
The reliability of a substrate curvature-based stress measurement method for CrN thin films on substrate with fluctuant surface was discussed.The stress error led by the ignorance of substrate thermal deformation was studied.Results showed that this error
Using the methods of transmission electron microscopy,the carbide phase evolution in surface layers of the differentially quenched rails is studied after the passed tonnage of 691.8 million tons at the depth up to 10 mm along the central axis and fillet o
The effect of heat treatment on the microstructures and mechanical properties of a newly developed austenitic heat resistant steel (named as T8 alloy) for ultra-supercritical applications have been studied.Results show that the main phases in the alloy af
A reaction interface between the aluminum and K2ZrF6 during molten salt reaction process was frozen by quenching the mold in water,and the interface structure was analyzed to determine the formation process of Al3Zr.Results show that a clear conical inter
A turtle carapace bio-inspired Ti matrix hybrid composite was successfully fabricated in this work. This composite incorporates two parts: the Ti-Al intermetallic multilayered composite and continuous SiC fibers-reinforced Ti matrix composite. In the Ti-A
Electropulsing-induced phase decompositions and microstmctural changes in AZO-5 thin films were studied by X-ray diffraction,scanning electron microscopy,atomic force microscopy,Hall effect measurement and photoluminescence (PL)measurement techniques.It w