A new anodic material of ternary Pb-0.8%Ag-(0-5.0%)Bi alloy for zinc electrowinning was obtained by doping Bi.The anodic oxygen evolution potential,corrosion rate,surface products after polarization,and microstructures before and after polarization were studied and compared with those of Pb-0.8%Ag anode used in industry.The results show the anodic overpotential decreases with the increase of Bi content in the alloys.When the content of Bi is 1.0%(mass fraction),the anodic overpotential is 40-50 mV lower than that of Pb-0.8%Ag anode.While the corrosion rate decreases and then increases with the increase of Bi content.The Pb-0.8%Ag-0.1%Bi anode has the lowest corrosion rate(0.090 6 mg/(h·cm2).Doping Bi influences the structure of the anodic layer,but does not change the phase.The Pb-0.8%Ag-1.0%Bi anode layer is of a more fine-grained structure compared with Pb-0.8%Ag anode.
A new anodic material of ternary Pb-0.8% Ag- (0-5.0%) Bi alloy for zinc electrowinning was obtained by doping Bi. Anodic oxygen evolution potential, corrosion rate, surface products after polarization, and microstructures before and after polarization were studied and compared with those of Pb-0.8% Ag anode used in industry. results show the anodic overpotential decreases with the increase of Bi content in the alloys. WHERE the content of Bi is 1.0% (mass fraction), the anodic overpotential is The percentage of 40-50 mV lower than that of Pb-0.8% Ag anode. Whilst the corrosion rate decreases and then increases with the increase of Bi content. Pb-0.8% Ag-0.1% Bi anode has the lowest corrosion rate (0.090 6 mg /(h?cm2). Doping Bi influences the structure of the anodic layer, but does not change the phase. Pb-0.8% Ag-1.0% Bi anode layer is of a more fine- grained structure compared with Pb-0.8% Ag anode.