【摘 要】
：
我厂新产品φ2000M牵引轮中的推线环铸件(见图1),材质为HT20-40,毛重450kg。开始生产时,铸件常出现图2所示的裂纹,裂纹长约500mm,深5～15mm,宽6～12mm。观察铸件裂纹,发现裂口表
论文部分内容阅读
我厂新产品φ2000M牵引轮中的推线环铸件(见图1),材质为HT20-40,毛重450kg。开始生产时,铸件常出现图2所示的裂纹,裂纹长约500mm,深5～15mm,宽6～12mm。观察铸件裂纹,发现裂口表面呈氧化色,裂口中还有石墨化膨胀时挤出的小铁豆,经分析认为是热裂。导致铸件产生热裂的主要原因是浇
I plant new products φ2000M traction wheel push ring castings (see Figure 1), made of HT20-40, gross weight 450kg. At the beginning of production, the casting often shows the crack shown in Figure 2, the crack length is about 500mm, depth 5 ~ 15mm, width 6 ~ 12mm. Casting cracks were observed and found that the surface of the crack was oxidized color, there are cracks in the graphite extrusion expansion of small iron beans, the analysis that is hot cracking. The main reason leading to casting hot cracking is pouring
其他文献
目前刷镀均采用不溶性阳极——石墨进行刷镀,本文较为详细地介绍了江汉石油管理局运输公司人修厂,采用可溶性金属阳极在刷镀应用中的优缺点,并介绍他们研制出的几种适用于可
本文从力学上分析了叶片锻模产生开裂的原因,计算实际锻造时模具所受的应力,修正锻造角,使得其所受水平侧向力在允许范围内,以延长模具使用寿命
In this paper, the causes
Cr 12型解包括Cr 12、Cr 12W、Cr 12 MoV。它们均属于莱氏体合全工具钢。在铸态时具有网状共晶组织。冶金厂供应的Cr 12型钢均为轧制状态,虽然碳化物已有一定程度的破碎,但
国外铸造生产中,近十年来广泛应用自硬砂造型、制芯工艺。它在铸件质量、劳动量、劳动条件、节能等方面显示了巨大优越性。上海汽轮机厂1979年试用呋喃自硬砂生产了300MW汽
1.前言预热器的作用通常是利用加热炉排出的高温烟气将煤气或空气预热到适当的温度,使煤气或空气进入炉内燃烧或助燃时带入一部分物理热,以节约燃料和提高燃烧温度。众所周
为了鼓励学生创业,衢州中专近日在学校艺术楼大礼堂内开设了创业讲座。“你想做什么?你能做什么?你要怎么做?”衢州中专实训与指导中心副主任郑军的一串问题,让现场同学陷入
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
没有了擎天柱姚明火箭将士依然踌躇满志从1号变身为3号麦迪期待着职业生涯的新生
Without Optimus Prime Yao Ming rocket officers still proud of No. 1 transformed from
炭疽为一种人、善共患急性传染病,部分国家将炭疽杆菌作为生物威胁因子进行研究和生产。该菌毒性与质粒PXO1、PXO2有关,PXO1产物包括水肿因子、保护性抗原和致死因子。PXO2是
轧辊表面经滚痕加工形成辊面沟痕,如图1所示,在轧钢时可提高轧辊与金属间摩擦系数,可改善咬入条件。轧辊经滚痕冷加工后,表层得到强化,表面硬度提高,从而还可提高轧辊使用寿