异种金属1Cr18Ni9Ti和GH3044在点焊后X光检查时发现裂纹。通过对焊点进行金相检查、断口观察和电镜能谱分析后表面发现:焊缝组织为单相奥氏体组织,裂纹断口为典型焊接热裂纹
论文部分内容阅读
异种金属1Cr18Ni9Ti和GH3044在点焊后X光检查时发现裂纹。通过对焊点进行金相检查、断口观察和电镜能谱分析后表面发现:焊缝组织为单相奥氏体组织,裂纹断口为典型焊接热裂纹形貌,焊点中镍含量较高。经过分析验证得出结论:由于焊接过程中GH3044熔入量大,导致焊缝中镍含量增大,形成单相奥氏体组织,产生焊接热裂纹。
The dissimilar metals 1Cr18Ni9Ti and GH3044 show cracks after X-ray inspection after spot welding. The metallographic examination of solder joint, fracture observation and electron microscopy analysis showed that the weld microstructure was single-phase austenite, the fracture surface was a typical hot weld crack, and the nickel content in the weld joint was high. After the analysis and verification, it is concluded that due to the large amount of GH3044 melted in the welding process, the nickel content in the weld increases, forming a single-phase austenite structure, resulting in a weld hot crack.
其他文献
肝硬化患者由于其自身代谢特点,胆囊结石患病率较高,约为非肝硬化患者的8倍.由于此类患者肝功能异常导致凝血功能异常、蛋白质合成功能下降、门静脉高压等,使得腹腔镜胆囊切
为了合理使用抗菌药物,减少药物不良反应发生率,我们对我院2007年1月-2011年12月发生的535例抗菌药物不良反应进行了回顾性分析。现报告如下。1临床资料
In order to ration
1病例报告患者女,75岁。因上腹痛,伴有呼吸困难4 h入院。4 h前无诱因出现上腹痛,呈剑下及左上腹持续性胀痛,放射至胸骨后下段,阵发性加剧;伴呼吸困难,胸闷、气促、大汗,无发
经自然腔道内镜外科手术(NOTES),是指经由人体与外界自然相通的开口或管腔(口腔、鼻腔、肛门、阴道和尿道等),将内镜器械通过切口或穿刺孔置入体腔进行操作的手术类型。由于
咳嗽变异型哮喘(CVA)又称咳嗽性哮喘,是一种特殊类型的哮喘.以顽固性咳嗽为主要临床表现,由于无喘息症状,极易误诊.2010年3月-2012年10月,我们共收治咳嗽变异型哮喘19例,现将
美国结束超宽松货币政策的时机与国际效应、美国财政赤字周期性“发酵”的效应、欧元区债务及东亚日本引出的问题,或将成为影响2014年全球经济的不确定因素经济运行受两类因
慢性咽炎临床可表现为咽部所有不适症状,如疼痛、烧灼感、发干、堵塞、异物感、憋闷感、干咳、咽喉发痒及异味感等.对于出现上述咽部不适症状的患者,应结合专科检查,根据其咽
目的:观察不同剂量丙泊酚用于复合麻醉诱导时对循环系统的影响.方法:择期全麻手术150例,随机分为A、B、C3组各50例.麻醉诱导采用不同剂量的丙泊酚复合咪达唑仑、芬太尼、维库
2014年两会的政府工作报告,是贯彻落实党的十八届三中全会和中央经济工作会议确立深化改革的具体部署之后的第一次政府工作报告。整个报告准确把握了各方对改革的需求,明确了
本文报告了某警卫部队机关门诊部根据其服务功能和工作特点,在坚定信念、严格纪律、提高专业技能、改善医疗条件、营造温馨环境等方面加强管理,努力改进医疗服务的做法.