The Tb40(Fe49Co49V2)60 films were fabricated by magnetron cosputtering from a multiple target arrangement at different argon pressures.The samples were investigated using X-ray diffraction,magnetic force microscope and vibrating sample magnetometer.A strong perpendicular anisotropy was obtained for the sample prepared at 0.4 Pa.The easy direction of magnetization could be turned from perpendicular to in-plane direction either at high working pressures(P Ar >2.0 Pa) or by annealing at temperatures higher than 250 °C.An excellent magnetic softness with coercivity below 3 mT and saturating field of 20 mT in film-plane direction was obtained for the sample prepared at 0.7 Pa and then annealed at 350 °C.
The Tb40 (Fe49Co49V2) 60 films were fabricated by magnetron cosputtering from a multiple target arrangement at different argon pressures. The samples were investigated using X-ray diffraction, magnetic force microscope and vibrating sample magnetometer. A strong perpendicular anisotropy was obtained for the sample prepared at 0.4 Pa. The easy direction of magnetization could be turned from perpendicular to in-plane direction either at high working pressures (P Ar> 2.0 Pa) or by annealing at temperatures higher than 250 ° C. An excellent magnetic softness with coercivity below 3 mT and saturating field of 20 mT in film-plane direction was obtained for the sample prepared at 0.7 Pa and then annealed at 350 ° C.