论文部分内容阅读
Superplastic tensile tests of AlNp/606l Al Composites, fabricated by powder metallurgy techniques, were performed at strain rates ranging from 10-1-10-3S-1 and at temperatures from 833 to 893 K. Hot rolling after extrusion was employed to obtain a fine grained structure before superplastic testing. The superplastic behavior of AlNp/6061 Al Composites was compared with that of AlN particulate size. Differential scanning calorimeter was used to ascertain the possibility of any partial melting in the vicinity of optimum superplastic temperatures.