【摘 要】
：
针对ZG1Cr18Ni9Ti材质的铸造壳体在生产过程开裂的问题,通过金相手段对裂纹缺陷进行了分析,发现铸件基体晶界处存在聚集的氮化钛。通过与原材料金相进行对比,确定了这种氮化
论文部分内容阅读
针对ZG1Cr18Ni9Ti材质的铸造壳体在生产过程开裂的问题,通过金相手段对裂纹缺陷进行了分析,发现铸件基体晶界处存在聚集的氮化钛。通过与原材料金相进行对比,确定了这种氮化钛是在原材料重熔凝固为铸件时形成的。铸件厚大部位凝固缓慢,导致氮化钛在晶界大量聚集从而形成裂纹源,在后续冷热加工应力的作用下壳体从晶界开裂。
In view of the cracking problem of ZG1Cr18Ni9Ti cast shell in the production process, the crack defects were analyzed by metallography, and it was found that the aggregated titanium nitride exists in the grain boundary of the casting base. By comparing with the raw material metallography, it is confirmed that the titanium nitride is formed when the raw material is remelted and solidified into a casting. Casting large parts of the solidification slow, resulting in a large number of titanium nitride aggregation in the grain boundary to form a source of cracks in the subsequent hot and cold processing stress under the action of shell cracking from the grain boundary.
其他文献
吴悦石作品包头地区总代理联系地址:内蒙古包头市昆区锡华丹青苑商业街18号宝文斋联系电话:0472-5910468 13904724899(冀先生)18747212080(李女士)电子信箱:baowenzhaihl@163
随着老龄化社会进程的加快,老年人身体健康状况备受人们关注。太极拳有其独特的运动特点,是老年人强身健身的首选项目之一。文章采用文献资料法、实地考察法等进行研究,在分
堆焊是一种常规的涂层制备方法,并且制备的涂层可以满足各种性能要求的需要。堆焊在工业中普遍应用,然而,他们有一个共同点,由于涂层制备速度的限制,导致成本相对较高。本文
作为全球打印耗材行业一年一度的国际盛会,第五届亚洲打印耗材展览会于2008年11月10-12日在上海展览中心如期举行。本届展会的规模再创历史新纪录,在19.000平方米的展区内,共
利用扫描电子显微镜、透射电子显微镜和力学压缩试验机研究热处理工艺对Ni42Ti8Al合金微观组织和力学性能的影响。结果表明,铸态Ni42Ti8Al合金由Ni Ti基体和晶界网状共晶体组
本文综述北部湾东北部R_1孔岩心记录。R_1孔岩心长度100m,水深42m。在粒度分析、矿物分析及微体古生物分析的基础上,认为该区在上新世时,为浅海相沉积,更新世则以陆相为主,仅
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
近年来,高职教育的发展越来越受到政府、家长、学生及各用人单位的重视。高职教育的转型为高职英语教师的职业发展提供了契机和挑战,如何定位自己未来的职业发展方向,是高职
First principles calculations are carried out to investigate the structural stability of several non-equilibrium intermetallic phases in the cobalt(Co)–Mo syst
日前,从江苏检验检疫局传来消息,连云港振兴恒巨生物科技有限公司获得国家出口种苗企业备案资格,成为连云港市首家具有出口资质的花卉企业。
Recently, news came from Jian