DISCUSSION ON DEFECTS DISTRIBUTION NEAR THE STEEL SURFACE IRRADIATED BY INTENSE PULSED ION BEAM

• 作 者: X.Y. Le\\r\\r\\r\\r\\r\\r\\r\\r\\r\\n S. Yan\\r\\r\\r\\r\\r\\r\\r\\r\\r\\n W.J. Zhao \\r\\r\\r\\r\\r\\r\\r\\r\\r\\n B.X. Han \\r\\r\\r
• 出 处: Acta Metallurgica Sinica(English Edition)
• 发表日期: 2002年01期
• 关键词: stainless SURFACE irradiated defects dynamical acceleration pulsed microhardness

The surface defect distribution in stainless steel irradiated with intense pulsed ion beam (IPIB) of current density above 60A/cm2 and acceleration voltage 300-500keV was discussed and analyzed. The defects near the surface of stainless steel were generated in two ways: (1) generated by the bombardment of energetic ions and (2) induced by the high level stress near the surface. Thus the temperature and stress distributions near the steel surface were calculated by means of our STEIPIB code, which treated with the thermal-dynamical process in the target irradiated by the IPIB. Based on these distributions, the generations and movements of these defects were discussed and compared with the experiment results.

The surface defect distribution in stainless steel irradiated with intense pulsed ion beam (IPIB) of current density above 60 A / cm2 and acceleration voltage 300-500 keV was discussed and analyzed. The defects near the surface of stainless steel were generated in both ways: (1 generated by the bombardment of energetic ions and (2) induced by the high level stress near the surface. Thus the temperature and stress distributions near the steel surface were calculated by means of our STEIPIB code, which treated with the thermal-dynamical process in the target irradiated by the IPIB. Based on these distributions, the generations and movements of these defects were discussed and compared with the experiment results.