【摘 要】
：
在叶片生产中,叶身与叶根连接处的成形为叶片辊锻工艺的关键技术之一。对于带有叶根的叶片,为了成形和操作方便,常采用逆辊成形。叶根在送料的一边,如图1所示。坯料开始变形
论文部分内容阅读
在叶片生产中,叶身与叶根连接处的成形为叶片辊锻工艺的关键技术之一。对于带有叶根的叶片,为了成形和操作方便,常采用逆辊成形。叶根在送料的一边,如图1所示。坯料开始变形时,模具直接压入坯料,这样在叶身与叶根过渡处形成一斜角区域,这部分我们称之为压入角区。 1、辊锻叶片压入角区的形成压入角区是怎么形成的呢?图1为叶片辊
In the blade production, the formation of the blade body and the blade root connection is one of the key technologies of the blade roll forging process. For leaves with leaves, in order to shape and easy to operate, often using reverse roll forming. Leaf root in feeding side, shown in Figure 1. When the billet starts to deform, the mold is pressed directly into the billet, thus forming a bevel region at the transition of the blade body and the root of the blade. This part is called the press-in angle region. 1, roll forging blade into the formation of angle into the corner area is how to form it? Figure 1 for the blade roll
其他文献
研究了09V钢热轧工艺参数对奥氏体及铁素体晶粒的影响及铁素体晶粒对韧性的影响,以及冷速与组织性能的相互关系。试验结果表明:铁素体晶粒细化10μm,可使脆性转化温度下降8℃
一般用来制造本体直径>1100mm的大型发电机转子(钢锭重量>100t)的25XH3MΦA钢(相相于25CrNi3MoV钢),最近已开始用于汽轮机的轴类和轮盘、65000tf水压机、170压力机高负荷的
Ｌｅ“ｑｕｅ‘”ｃｏｎｓéｃｕｔｉｆｄéｓｉｇｎｅｌａｃｏｎｊｏｎｃｔｉｏｎ“ｑｕｅ”ｄａｎｓｌｅｓｐｒｏｐｏｓｉｔｉｏｎｓｃｏｎｓéｃｕｔｉｖｅｓｉｎｔｒｏｄｕｉｔｅｓｐａｒｌｅｓｅｘｐｒｅｓｉｏｎｓ“ｔｅｌｅｍｅｎｔ．．．ｑｕｅ；ｔａｎｔ．．．ｑ...
Le “que” “consécutifdésignelaconjonction” que “danslespropositionsconscutivestroduitesparlesexpresions” telement ... que; tan
11月底,冲电气工业株式会社(简称OKI)和日冲商业(北京)有限公司宣布,在中国市场推出面向100人以下办公环境使用、具备IP电话功能及移动电话功能的新型业务电话设备IPstage MX
光谱分析检出限是评价光谱仪器性能和分析方法的一项重要指标。长期以来人们对它的概念不清,使用混乱。七十年代国内曾在《分析化学》上展开过讨论,最后黄本立同志介绍了国
采用酶解沉降法将碘含量为6mol％的多分散的溴碘化银乳剂分成9个级份,测量各个级份的乳剂在不同温度下的离子电导率,求出它们的离子电导活化能和表面空间电荷层的特性参数。发
一、引言现今浇铸镇静钢,国内外已广泛应用绝热板代替耐火粘土砖内衬保温帽。钢锭切头率已从15～18％降低到8～12％工,可使钢锭成坯、成材率提高3～8％。1982年上半
I. INTRODUCTION No
我们根据无强迫联系双轴落砂机的运动机理,在北京电机厂设计制造了一台采用振动电机组合驱动的双轴落砂机(外形见图1),并成功地用于4～7电机座铸件的落砂。该机与其它双轴落砂
斜轧成形工艺是一种生产效率高,材料利用率高的少无切屑新工艺。这项新工艺日益受到人们的重视,并且得到较迅速的发展。所谓斜轧成形,是指数个相互倾斜配置的轧辊,当其同方
在加工过程中对工件的尺寸进行主动测量,是一种先进的检测形式,它能主动控制加工过程,确保产品质量,也是提高劳动生产率的一种有力手段。目前主动测量装置国内外都广泛应用