Vanadium oxide thin films were prepared on glass substrates by using the spray pyrolysis technique.The effect of solution concentration(0.1 M,0.2 M and 0.3 M) on the nanostructural,electrical,optical,and electrochromic properties of deposited films were investigated using X-ray diffraction,scanning electron microscopy,UV–vis spectroscopy,and cyclic volta-metrics.The X-ray diffraction shows that only the sample at 0.1 M has a single β-V2O5phase and the others have mixed phases of vanadium oxide.The lowest sheet resistance was obtained for the samples prepared at 0.3 M solution.It was also found that the optical transparency of the samples changes from 70% to 35% and the optical band gap of the samples was in the range of 2.20 to 2.41 eV,depending on the morality of solution.The cycle voltammogram shows that the sample prepared at 0.3 M has one-step electerochoromic but the other samples have two-step electerochoromic.The results show a correlation between the cycle voltammogram and the physical properties of the films.
Vanadium oxide thin films were prepared on glass substrates by using the spray pyrolysis technique. The effect of solution concentration (0.1 M, 0.2 M and 0.3 M) on the nanostructural, electrical, optical, and electrochromic properties of deposited films were investigated using X- ray diffraction, scanning electron microscopy, UV-vis spectroscopy, and cyclic volta-metrics. X-ray diffraction shows that only the sample at 0.1 M has a single β-V2O5phase and the others have mixed phases of vanadium oxide.The lowest sheet was found for the samples prepared at 0.3 M solution. It was also found that the optical transparency of the samples changes from 70% to 35% and the optical band gap of the samples was in the range of 2.20 to 2.41 eV, depending on the morality of solution. The cycle voltammogram shows that the sample prepared at 0.3 M has one-step electerochoromic but the other samples have two-step electerochoromic. The results show a correlation between the cycle voltammogram and t he physical properties of the films.