The content of zirconia has a remarkable influerce on transformation behavior and mechanical properties of Al2O3/ZrO2 (2Y) composites. When 15% and 20% ZrO2(2Y) was added to Al2O3, the bending strength and fracture of the content of ZrO2 (2Y) on transformation and mechanical properties was investigated. The changes of m-ZrO2 and t-ZrO2 phases content before and after fracture were measured by X-ray diffraction quantitative phase analysis, It is shown that improvement in bending strength and fracture toughness of the Al2O3/ ZrO2 (2Y) composites is due to the phase transformation toughening mechanism of ZrO2 (2Y) and thermal expansion mismatch.