【摘 要】
：
Hydroxyapatite powder was prepared by sol-gel method using the calcium nitrate tetrahydrate and pentoxide as reactant. The effects of main processing parameters
【机 构】
：
Shandong Electric Power Research Institute,Department of Materials Science and Engineering
论文部分内容阅读
Hydroxyapatite powder was prepared by sol-gel method using the calcium nitrate tetrahydrate and pentoxide as reactant. The effects of main processing parameters such as reagent, concentration, temperature etc on the synthesis of hydroxyapatite were investigated. The synthetic mechanism was also studied. The results showed that main optimized parameters were as follows: 2 M ethanol solution of P2 O5 and 4 M ethanol solution Ca( NO3 )2 ·4H2 O, 12-24 h of aging time, 500 ℃ sintered temperature. X-ray diffraction and Fourier transform infrared spectra results showed that the mixtures were composed of amorphous hydroxyapatite, Ca ( NO3 )2,PO(OH)3-x(OR)x, bellow 400 ℃ . The pure hydroxyapatite powder were prepared at 500 ℃ for 30 min.The aging of the sol influenced the purity greatly. The CaO phase was observed from the powder without aging.This process with cheap reactants was simple and the advantages offered by this process made it possible to produce the uniform fine powder in large quantity.
其他文献
The main cause to the deactivation of ZSM-5 catalyst, used for oxidation of benzene to phenol (BTOP)by nitrous oxide, is that the carbon deposition on the catal
Homogeneous HA coating materials were prepared on porous titanium by the low-temperature combustion synthesis. It was found that the mechanical properties of th
A novel bifunctional dye containing spirobenzopyran and cinnamoyl moiety has been prepared and its photochromic behavior following irradiation at different wave
The bioactive α-Ca3 (PO4)2 bone cement was studied by XRD , SEM and isothermal calorimetric measurements. The results showed that a mixed pattern of TCP and hy
The bonding of solid steel plate to liquid aluminum was studied using rapid solidification. The relationship models of interfacial shear strength and thickness
The aim of this work was to produce a nanoscale fluoridated and potassium containing hydroxyapatite via sol-gel method and to observe the effect of occlusion of
Three cement samples were prepared, including OPC consisted of 100wt% portland cement, PFA consisted of 70wt% portland cement and 30wt% fly-ash, and CA consiste
In recent years,materials with ultrafine grain size(UFG) have attracted much attention.By using severe plastic deformation(SPD) techniques,materials with fine g
The distribution of microelement Fe, Si, Cu and Mg in the surface layer of aluminum foil annealed at 300℃ and 500℃ were determined by secondary ion mass spect
With the help of an electromagnetic stirring device self-made and alloy melt quenching technology,the effect of electromagnetic stirring parameters on the micro