【摘 要】
：
In this investigation, protective layers were formed on aluminum substrate by Plasma Electrolytic Deposition (PED) using sodium silicate solution. The relation
【机 构】
：
Institute of Mechanics
论文部分内容阅读
In this investigation, protective layers were formed on aluminum substrate by Plasma Electrolytic Deposition (PED) using sodium silicate solution. The relation between the thickness of the layer and process time were studied. XRD,SEM, EDS were used to study the layers structure, composition and micrograph. The results show that the deposited layers are amorphous and contain mainly oxygen, silicon, and aluminum. The possible formation mechanism of amorphous [Al-Si-O] layer was proposed: During discharge periods, Al2O3 phase of the passive film and SiO32-near the substrate surface are sintered into xSiO2(1-x)Al2O3 and then transformed into amorphous [Al-Si-O] phase.
其他文献
The method of designing industrial processes of quench cooling, in particular, the speed of the conveyor movement with regard to shape and sizes of parts to be
Excellent mechanical properties are obtained by austempering after hot deformation without subsequent heat treatment in the present Si-Mn TRIP steel sheets. Iso
The cross-sectional indentation method is extended to evaluate the interfacial adhesion between brittle coating and ductile substrate. The experimental results
Phosphate coatings are partially dissolved in the cathodic area during the cathode-electrophoretic painting processes causing the result that the coatings adhes
Engineering the surfaces of components to improve the life and performance of parts used in automotive and aerospace engineering is the active area of research.
Application of magnetic flux controllers/concentrators to induction heating coils can drastically improve the process efficiency and heat pattern control. Prese
以吡啶和1-溴代正辛烷为原料,制得中间产物α-辛基吡啶,再分别与1,4-二溴丁烷和1,6-二溴己烷反应,得到两种含氮杂环的双子季铵盐表面活性剂,通过定性实验和波谱方法鉴定了其
在单模光纤中,输入的激光功率大于阈值时,出现放大的反斯托克斯拉曼背向自发散射现象.实验发现:放大的反斯托克斯拉曼背向自发散射具有温度效应,与反斯托克斯拉曼背向自发散
研究驻波型激光脉冲作用下,失谐量足够大时,囚禁于Paul阱中的单离子系统的久期运动.通过分析和数值计算相结合的方法,导出系统的精确解及其描述的时间演化性质,得到系统的规
本文采用电子回旋共振微波等离子体化学气相沉积方法 (ECR -CVD) ,以CH4和H2 为气源、Fe3 O4纳米粒子为催化剂 ,未加电场 ,在多孔硅基底上制备出大面积取向生长碳纳米管。使